RESUMEN
Harnessing the inexhaustible solar energy for water splitting is regarded one of the most promising strategies for hydrogen production. However, sluggish kinetics of oxygen evolution reaction (OER) and expensive photovoltaics have hindered commercial viability. Here, an adhesive-free electrodeposition process is developed for in-situ preparation of earth-abundant electrocatalysts on super-flat indium tin oxide (ITO) substrate. NiFe hydroxide exhibited prominent OER performance, achieving an ultra-low overpotential of 236 mV at 10 mA/cm2 in alkaline solution. With the superior OER activity, we achieved an unassisted solar water splitting by series connected perovskite solar cells (PSCs) of 2 cm2 aperture area with NiFe/ITO//Pt electrodes, yielding overall solar to hydrogen (STH) efficiency of 13.75 %. Furthermore, we upscaled the monolithic facility to utilize perovskite solar module for large-scale hydrogen production and maintained an approximate operating current of 20 mA. This creative strategy contributes to the decrease of industrial manufacturing expenses for perovskite-based photovoltaic-electrochemical (PV-EC) hydrogen production, further accelerating the conversion and utilization of carbon-free energy.
RESUMEN
The two-step sequential deposition strategy has been widely recognized in promoting the research and application of perovskite solar cells, but the rapid reaction of organic salts with lead iodide inevitably affects the growth of perovskite crystals, accompanied by the generation of more defects. In this study, the regulation of crystal growth was achieved in a two-step deposition method by mixing 1-naphthylmethylammonium bromide (NMABr) with organic salts. The results show that the addition of NMABr effectively delays the aggregation and crystallization behavior of organic salts; thereby, the growth of the optimal crystal (001) orientation of perovskite is promoted. Based on this phenomenon of delaying the crystallization process of perovskite, the "slow-release effect assisted crystallization" is defined. Moreover, the incorporation of the Br element expands the band gap of perovskite and mitigates material defects as nonradiative recombination centers. Consequently, the power conversion efficiency (PCE) of the enhanced perovskite solar cells (PSCs) reaches 20.20%. It is noteworthy that the hydrophobic nature of the naphthalene moiety in NMABr can enhance the humidity resistance of PSCs, and the perovskite phase does not decompose for more than 3000 h (30-40% RH), enabling it to retain 90% of its initial efficiency even after exposure to a nitrogen environment for 1200 h.
RESUMEN
Defect passivation of the perovskite surface and grain boundary (GBs) has become a widely adopted approach to reduce charge recombination. Research has demonstrated that functional groups with Lewis acid or base properties can successfully neutralize trap states and limit nonradiative recombination. Unlike traditional Lewis acid-base organic molecules that only bind to a single anionic or cationic defect, zwitterions can passivate both anionic and cationic defects simultaneously. In this work, zwitterions organic halide salt 1-amino pyridine iodine (AmPyI) is used as a perovskite for defect passivation. It is found that a pair of amino lone electrons in AmPyI can passivate defects surface and GBs through hydrogen bonding with perovskite, and the introduced I- can bind to uncoordinated Pb2+ while also controlling the surface morphology of the film and improving the crystallinity. In the presence of the AmPyI additive, we obtained about 1.24 µm of amplified perovskite grains and achieved an efficiency of 23.80% with minimal hysteresis.