RESUMEN
Using synchrotron based photoemission, we have investigated the Mn-induced changes in Ga 3d core level spectra from as-grown Ga(1-x)Mn(x)As. Although Mn is located in Ga substitutional sites, and therefore does not have any Ga nearest neighbors, the impact of Mn on the Ga core level spectra is pronounced even at Mn concentrations in the region of 0.5%. The analysis shows that each Mn atom affects a volume corresponding to a sphere with around 1.4 nm diameter.
RESUMEN
Thermally stimulated diffusion of Mn through thin layers of GaAs has been studied by x-ray photoemission. (Ga, Mn)As samples with 5 at% Mn were capped with 4, 6 and 8 monolayer (ML) GaAs, and Mn diffusing through the GaAs was trapped on the surface by means of amorphous As. It was found that the out-diffusion is completely suppressed for an 8 ML thick GaAs film. The short diffusion length is attributed to an electrostatic barrier formed at the (Ga, Mn)As/GaAs interface.