RESUMEN
Combining theory with experiments, we study the phase stability, elastic properties, electronic structure and hardness of layered ternary borides AlCr2B2, AlMn2B2, AlFe2B2, AlCo2B2, and AlNi2B2. We find that the first three borides of this series are stable phases, while AlCo2B2 and AlNi2B2 are metastable. We show that the elasticity increases in the boride series, and predict that AlCr2B2, AlMn2B2, and AlFe2B2 are more brittle, while AlCo2B2 and AlNi2B2 are more ductile. We propose that the elasticity of AlFe2B2 can be improved by alloying it with cobalt or nickel, or a combination of them. We present evidence that these ternary borides represent nanolaminated systems. Based on SEM measurements, we demonstrate that they exhibit the delamination phenomena, which leads to a reduced hardness compared to transition metal mono- and diborides. We discuss the background of delamination by analyzing chemical bonding and theoretical work of separation in these borides.
RESUMEN
We have studied alloying of the nonmagnetic spacer layer with a magnetic material as a method of tuning the interlayer coupling in magnetic multilayers. We have specifically studied the Fe/V(100) system by alloying the spacer V with various amounts of Fe. For some Fe concentrations in the spacer, it is possible to create a competition between antiferromagnetic Ruderman-Kittel-Kasuya-Yoshida exchange and direct ferromagnetic exchange coupling. The exchange coupling and transport properties for a large span of systems with different spacer concentrations and thicknesses were calculated and measured experimentally and good agreement between observations and theory was observed. A reduction in magnetoresistance of about 50% was observed close to the switchover from antiferromagnetic to ferromagnetic coupling.