RESUMEN
The corrosion of concrete in sulfate environments is a difficult problem in the durability of civil engineering structures. To investigate the variability of deterioration damage to concrete structures by sulfate erosion under non-destructive testing and quantify the protective effect of silane coatings on concrete under the action of sulfate erosion, an accelerated erosion experiment was carried out using field sampling in a tunnel project under a sulfate erosion environment. By means of ultrasonic velocity measurement and CT scanning, the samples protected by a silane coating under the sulfate attack environment were compared with those not protected. The deterioration characteristics of concrete under the sulfate attack environment and the protective effect of silane coating on the concrete structure were analyzed. In addition, a method for evaluating the sulfate damage to concrete based on CT images and ultrasonic velocity analysis was proposed. The results show that the samples prepared in the field show a significant difference in ultrasonic velocity in the process of erosion and deterioration according to the material difference at the measuring point interface. Through the overall damage evaluation analysis of the sample, it is concluded that the damage degree of the protected group sample is light and the heterogeneity is weak, whereas the local damage to the exposed group is serious. Combined with the CT image analysis of concrete before and after loading, the distribution characteristics of the damaged area divided by the concrete sulfate damage evaluation method proposed in this paper are highly similar to the real situation. The results of the study can provide a reference for similar projects for the detection, analysis, protection and evaluation of sulfate-attacked concrete.
RESUMEN
In order to study the protection performance of silane coating on in-service concrete structures in a sulfate environment, we collect concrete samples in the field to simulate the concrete erosion process by accelerated erosion with wetting-drying cycles. We place the samples into protected, exposed and control groups corresponding to a corrosive environment with silane protection, corrosive environment without protection and general environment for three different service conditions. A combination of ultrasonic velocimetry, CT (Computed Tomography) scan imaging, NMR (Nuclear Magnetic Resonance) pore structure analysis, strength testing and other methods are used to analyze the strength, ultrasonic wave velocity, pore structure and other characteristics of the specimens during sulfate erosion. Based on the test results, the protective effect of silane coating on concrete structures under sulfate attack is quantitatively analyzed, and an index for judging the damage rate of specimens is proposed to quantitatively analyze the protective effect of silane coating. The research results show that the damage of the concrete structure under silane protection in a sulfate-attack environment can be reduced by more than 50%; its integrity damage index and strength damage index are easily affected by the location of local defects, which leads to a decrease in the protection efficiency of the surface silane coating.
RESUMEN
Machine-made sand instead of natural sand has become an inevitable choice for the sustainable development of the concrete industry. Orthogonal experiment and grey correlation analysis were used to investigate the performance of machine-made tuff sand concrete. The optimal concrete mix ratio of machine-made sand was obtained by orthogonal test and its working performance was verified. Grey correlation analysis was applied to compare the factors affecting the mechanical properties of the machine-made sand concrete. The test results show that the sand rate has the greatest degree of influence on slump and slump expansion. The mineral admixture has the greatest effect on the 7-day compressive strength of the concrete. Additionally, the water-cement ratio has the greatest influence on the 28-day compressive strength. The mechanical and working properties of the machine-made sand concrete reach the optimum condition when the mineral admixture is 20%, the sand rate is 46%, the stone powder content is 10% and the water-cement ratio is 0.30. Comparing different fine aggregate concretes of similar quality, we conclude that the mechanical and working properties of tuff sand concrete and limestone sand concrete and river sand concrete are similar. The compressive strengths of the mechanism concrete show the greatest correlation with roughness and the least correlation with stone powder content. The stone powder content has almost no effect on the compressive strength of concrete when the stone powder content does not exceed a certain range. The results of the study point out the direction for the quality control of concrete with machine-made sand.
RESUMEN
Coarse aggregate in concrete is basically free from sulfate corrosion. If the influence of the coarse aggregate in the concrete is not eliminated, the change amount of the concrete ultrasonic pulse velocity value is directly used to evaluate the damage degree of sulfate corrosion in the concrete, and the results are often inaccurate. This paper presents an evaluation method of corrosion damage for the sulfate-attacked concrete by CT, ultrasonic velocity testing and AHP methods. CT was used to extract the coarse aggregate information in the specimen, and the proportion of coarse aggregate on the ultrasonic test line was calculated based on CT image analysis. Then, the correction value of ultrasonic pulse velocity (UPV) of the concrete structure was calculated, and the sulfate corrosion degree of concrete structure was evaluated using the analytic hierarchy process (AHP). The results show that the evaluation method proposed in this paper could more accurately evaluate the corrosion damage in the sulfate-attacked concrete structures, and the evaluation results were more in line with reality.
RESUMEN
Sulfate erosion is a major cause of concrete durability deteriorations, especially for the service tunnels that suffer sulfate erosion for a long time. Accurately predicting the concrete damage failure under sulfate erosion has been a challenging problem in the evaluation and maintenance of concrete structures. Here we design the dry-wet cycle test of service tunnel concrete under sulfate erosion and analyze the Elastic relative dynamic modulus (Erd) and mass under 35 times cycle periods. Then we develop an autoregressive integrated moving average (ARIMA) prediction model linking damage failure to Erd and mass. The results show that the deterioration of concrete first increased and then decreased with an extension of the dry-wet cycle period. Moreover, based on a finite set of training data, the proposed prediction approach shows high accuracy for the changes of concrete damage failure parameters in or out of the training dataset. The ARIMA method is proven to be feasible and efficient for predicting the concrete damage failure of service tunnels under sulfate erosion for a long time.
RESUMEN
With the continuous development of urbanization and industrialization in the world, concrete is widely used in various engineering constructions as an engineering material. However, the consequent problem of durability of concrete structures is also becoming increasingly prominent. As an important additional measure, a protective coating can effectively improve the durability of concrete performance. Moreover, the uniformity of the concrete surface coating will directly affect its protective effect. Therefore, we propose a nondestructive inspection and evaluation method of coating uniformity based on infrared imaging and cluster analysis for concrete surface coating uniformity detection and evaluation. Based on the obtained infrared images, a series of processing and analysis of the images were carried out using MATLAB software to obtain the characteristics of the infrared images of the concrete surface. Finally, by extracting the temperature distribution data of the pixel points on the concrete surface, an evaluation method of concrete surface coating uniformity based on a combination of cluster analysis and hierarchical analysis was established. The evaluation results show that the determination results obtained by this method are consistent with the actual situation. This study has a positive contribution to the testing of concrete surface coating uniformity and its evaluation.