A Single-Step Route to Robust and Fluorine-Free Superhydrophobic Coatings via Aerosol-Assisted Chemical Vapor Deposition.

Robust fluorine-free superhydrophobic films were produced from a mixture of two fatty acids (stearic acid and palmitic acid), SiO2 nanoparticles, and polydimethylsiloxane. These simple and nontoxic compounds were deposited via aerosol-assisted chemical vapor deposition to provide the rough topography required for superhydrophobicity, formed through island growth of the aggregates. The optimum conditions for well-adhered superhydrophobic films produced films with a highly textured morphology, which possessed a water contact angle of 162 ± 2° and a sliding angle of <5°. Superhydrophobicity was maintained after ultraviolet exposure (14 days at 365 nm), heat treatment (5 h at 300 °C and 5 h at 400 °C), 300 tape peel cycles, and exposure to ethanol and toluene (5 h each).

Production of an EP/PDMS/SA/AlZnO Coated Superhydrophobic Surface through an Aerosol-Assisted Chemical Vapor Deposition Process.

In this study, a superhydrophobic coating on glass has been prepared through a single-step aerosol-assisted chemical vapor deposition (AACVD) process. During the process, an aerosolized precursor containing polydimethylsiloxane, epoxy resin, and stearic acid functionalized Al-doped ZnO nanoparticles was deposited onto the glass at 350 °C. X-ray photoelectron spectroscopy, scanning electron microscopy, and atomic force microscopy showed that the precursor was successfully coated and formed a nano/microstructure (surface roughness: 378.0 ± 46.1 nm) on the glass surface. The coated surface had a water contact angle of 159.1 ± 1.2°, contact angle hysteresis of 2.2 ± 1.7°, and rolling off-angle of 1°, indicating that it was superhydrophobic. In the self-cleaning test of the coated surface at a tilted angle of 20°, it was shown that water droplets rolled and washed out dirt on the surface. The stability tests showed that the surface remained superhydrophobic after 120 h of exposure to ultraviolet (UV) irradiation and even after heat exposure at 350 °C. In addition, the surface was highly repellent to water solutions of pH 1-13. The results showed that the addition of the functionalized nanoparticles into the precursor allowed for the control of surface roughness and provided a simplified single-step fabrication process of the superhydrophobic surface. This provides valuable information for developing the manufacturing process for superhydrophobic surfaces.