In this paper, the zirconia (ZrO2) nanoparticles-based saturable-absorber (SA) have been incorporated in an erbium-doped fiber laser (EDFL) cavity for achieving a Q-switched pulse operation. The implementation of the zirconia nanoparticles-based powder on the fiber facet was accomplished using the index-matching gel's adhesion effect. The incorporation of SA in the laser cavity yielded a stable and self-starting Q-switched operation under 19.36 mW pump power that corresponded to the emission wavelength of 1557.29 nm. Additionally, it was observed that the EDFL's emission wavelength tuned from 1557.29 nm to 1562.3 nm , and the repetition rates and pulse width ranged from 61.2 to 130 kHz and 7.9 to 3.6 µs, respectively, as the pump power was increased from 19.36 to 380.16 mW. Measured experimental results reveal that at a maximum pump power of 380.16 mW, the maximum average output power, peak power, and pulse energy were noticed to be 1.17 mW, 2.5 mW, and 9 nJ, respectively. A 52 dB suppression in side bands was found at a pump power of 380.16 mW. Moreover, the stability and threshold tolerance of the EDFL has also been discussed in detail. These findings suggest that nanoparticle-based saturable absorbers have potential applications in a pulsed source, making it easier to implement in fiber cavity-based systems.
RESUMEN
This paper presents the investigations toward the direct use of bentonite clay (Al2H2O6Si) nanoparticles to act like a saturable absorber (SA) for the Q-switched pulse operation of an erbium-doped fiber laser (EDFL). The measured results reveal that with the incorporation of bentonite clay nanopowder as a SA, an EDFL is realized with a Q-switching mechanism starting at a pump power of 30.8 mW, and a Q-switched emission wavelength was noticed at 1562.94 nm at 142 mW pump power. With an increased pump from 30.8 mW to 278.96 mW, the temporal pulse parameters including minimum pulse duration and maximum pulse repetition rates were reported as 2.6 µs and 103.6 kHz, respectively. The highest peak power, signal-to-noise ratio, output power and pulse energy were noticed to be 16.56 mW, 51 dB, 4.6 mW, and 47 nJ, respectively, at a highest pump power of 278.96 mW. This study highlights the significance of bentonite clay (Al2H2O6Si) nanoparticles as a potential candidate for a saturable absorber for achieving nonlinear photonics applications.