RESUMEN
The development of short-wave infrared (SWIR) photonics based on GeSn alloys is of high technological interest for many application fields, such as the Internet of things or pollution monitoring. The manufacture of crystalline GeSn is a major challenge, mainly because of the low miscibility of Ge and Sn. The use of embedded GeSn nanocrystals (NCs) by magnetron sputtering is a cost-effective and efficient method to relax the growth conditions. We report on the use of GeSn/SiO2 multilayer deposition as a way to control the NC size and their insulation. The in situ prenucleation of NCs during deposition was followed by ex situ rapid thermal annealing. The nanocrystallization of 20×(11nm_Ge0.865Sn0.135/1.5nm_SiO2) multilayers leads to formation of GeSn NCs with â¼16% Sn concentration and â¼9 nm size. Formation of GeSn domes that are vertically correlated contributes to the nanocrystallization process. The absorption limit of â¼0.4 eV in SWIR found by ellipsometry is in agreement with the spectral photosensitivity. The ITO/20×(GeSn NC/SiO2)/p-Si/Al diodes show a maximum value of the SWIR photosensitivity at a reverse voltage of 0.5 V, with extended sensitivity to wavelengths longer than 2200 nm. The multilayer diodes have higher photocurrent efficiency compared to diodes based on a thick monolayer of GeSn NCs.
RESUMEN
GeSn alloys have the potential of extending the Si photonics functionality in shortwave infrared (SWIR) light emission and detection. Epitaxial GeSn layers were deposited on a relaxed Ge buffer on Si(100) wafer by using high power impulse magnetron sputtering (HiPI-MS). Detailed X-ray reciprocal space mapping and HRTEM investigations indicate higher crystalline quality of GeSn epitaxial layers deposited by Ge HiPI-MS compared to commonly used radio frequency magnetron sputtering (RF-MS). To obtain a rectifying heterostructure for SWIR light detection, a layer of GeSn nanocrystals (NCs) embedded in oxide was deposited on the epitaxial GeSn one. Embedded GeSn NCs are obtained by cosputtering deposition of (Ge1-xSnx)1-y(SiO2)y layers and subsequent rapid thermal annealing at a low temperature of 400 °C. Intrinsic GeSn structural defects give p-type behavior, while the presence of oxygen leads to the n-character of the embedded GeSn NCs. Such an embedded NCs/epitaxial GeSn p-n heterostructure shows superior photoelectrical response up to 3 orders of magnitude increase in the 1.2-2.5 µm range, as compared to performances of diode based only on embedded NCs.