RESUMEN
Self-healing concrete has the potential to optimise traditional design approaches; however, commercial uptake requires the ability to harmonize against standardized frameworks. Within EU SARCOS COST Action, different interlaboratory tests were executed on different self-healing techniques. This paper reports on the evaluation of the effectiveness of proposed experimental methodologies suited for self-healing concrete with expansive mineral additions. Concrete prisms and discs with MgO-based healing agents were produced and precracked. Water absorption and water flow tests were executed over a healing period spanning 6 months to assess the sealing efficiency, and the crack width reduction with time was monitored. High variability was reported for both reference (REF) and healing-addition (ADD) series affecting the reproducibility of cracking. However, within each lab, the crack width creation was repeatable. ADD reported larger crack widths. The latter influenced the observed healing making direct comparisons across labs prone to errors. Water absorption tests highlighted were susceptible to application errors. Concurrently, the potential of water flow tests as a facile method for assessment of healing performance was shown across all labs. Overall, the importance of repeatability and reproducibility of testing methods is highlighted in providing a sound basis for incorporation of self-healing concepts in practical applications.
RESUMEN
Cementitious composites are the most widely used construction materials; however, their poor durability necessitates frequent monitoring and repairs. The emergence of self-sensing composites could reduce the need for costly and time-consuming structural inspections. Natural graphite, due to its low cost and wide availability, is a promising additive to generate an electrically conductive network which could ultimately lead to a self-sensing mechanism. Despite several studies using natural graphite as a conductive additive, the effect of its fineness on the cementitious composite's performance has not been explored. This study experimentally investigated the effect of three graphite products of varying fineness on the early age, mechanical, and electrical conductivity performance of cement pastes. The fluidity of the graphite-cement paste reduced significantly with increasing graphite fineness, and graphite did not affect the cement hydration. The finer the graphite, the lower the effect on the mechanical performance, as confirmed by compressive strength testing and micro-indentation. Electrical conductivity testing showed that the percolation threshold depended on the graphite fineness and was found at ~20 wt % for the fine and medium graphite, while it increased to 30-40 wt % for the coarse graphite. This is the first study that has investigated holistically the effect of graphite fineness on the performance of cement pastes and will pave the way for using this material as an additive for self-sensing structures.
RESUMEN
Development and commercialization of self-healing concrete is hampered due to a lack of standardized test methods. Six inter-laboratory testing programs are being executed by the EU COST action SARCOS, each focusing on test methods for a specific self-healing technique. This paper reports on the comparison of tests for mortar and concrete specimens with polyurethane encapsulated in glass macrocapsules. First, the pre-cracking method was analysed: mortar specimens were cracked in a three-point bending test followed by an active crack width control technique to restrain the crack width up to a predefined value, while the concrete specimens were cracked in a three-point bending setup with a displacement-controlled loading system. Microscopic measurements showed that with the application of the active control technique almost all crack widths were within a narrow predefined range. Conversely, for the concrete specimens the variation on the crack width was higher. After pre-cracking, the self-healing effect was characterized via durability tests: the mortar specimens were tested in a water permeability test and the spread of the healing agent on the crack surfaces was determined, while the concrete specimens were subjected to two capillary water absorption tests, executed with a different type of waterproofing applied on the zone around the crack. The quality of the waterproofing was found to be important, as different results were obtained in each absorption test. For the permeability test, 4 out of 6 labs obtained a comparable flow rate for the reference specimens, yet all 6 labs obtained comparable sealing efficiencies, highlighting the potential for further standardization.
RESUMEN
A majority of well integrity problems originate from cracks of oil well cement. To address the crack issues, bespoke sodium silicate microcapsules were used in this study for introducing autonomous crack healing ability to oil well cement under high-temperature service conditions at 80 °C. Two types of sodium silicate microcapsule, which differed in their polyurea shell properties, were first evaluated on their suitability for use under the high temperature of 80 °C in the wellbore. Both types of microcapsules showed good thermal stability and survivability during mixing. The microcapsules with a more rigid shell were chosen over microcapsule with a more rubbery shell for further tests on the self-healing efficiency since the former had much less negative effect on the oil well cement strength. It was found that oil well cement itself showed very little healing capability when cured at 80 °C, but the addition of the microcapsules significantly promoted its self-healing performance. After healing for 7 days at 80 °C, the microcapsule-containing cement pastes achieved crack depth reduction up to ~58%, sorptivity coefficient reduction up to ~76%, and flexural strength regain up to ~27%. The microstructure analysis further confirmed the stability of microcapsules and their self-healing reactions upon cracking in the high temperature oil well cement system. These results provide a promising perspective for the development of self-healing microcapsule-based oil well cements.
RESUMEN
Pursuing long-term self-healing infrastructures has gained popularity in the construction field. Vascular networks have the potential to achieve long-term self-healing in cementitious infrastructures. To avoid further monitoring of non-cementitious tubes, sacrificial material can be used as a way of creating hollow channels. In this research, we report a new method for fabrication of complex 3D internal hollow tunnels using 3D printing of polyvinyl alcohol (PVA). The behaviour of 3D printed PVA structures in cement pastes was investigated using computed-tomography (CT) combined with X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), and scanning electron microscopy with energy dispersive spectroscopy (SEM/EDX). Results showed that (i) 1300 min were needed to fully dissolve 1 g of a 3D printed PVA structure, and different pH solutions did not significantly change the PVA dissolving process compared with a neutral environment; (ii) a low water/cement ratio can minimize early stage cracking resulting from PVA expansion; (iii) and PVA-cement interaction products were mainly calcite and a Ca-polymer compound. In conclusion, controlling the PVA expansion by decreasing the water/cement (w/c) ratio provides a promising approach to achieve 3D hollow channels in cement and, therefore, makes it possible to create complex tunnels within self-healing cementitious materials.