Unlocking the critical roles of N, P Co-Doping in MXene for Lithium-Oxygen Batteries: Elevated d-Band center and expanded interlayer spacing.

The design and fabrication of bifunctional catalysts with high electrocatalytic activity and stability are critical for developing highly reversible Li-O2 batteries (LOBs). Herein, the N, P co-doped MXene (NP-MXene) is prepared by one-step annealing method and evaluated as bifunctional catalyst for LOBs. The results suggest that the P doping plays a crucial role in increasing interlayer distance of MXene, thereby effectively providing more active sites, fast mass transfer, and ample space for the deposition/decomposition of Li2O2. Moreover, the N doping can significantly elevate the d-band center of Ti, thereby remarkably improving the adsorption of reaction intermediates and accelerating the deposition/decomposition of Li2O2 films. Consequently, the MXene-based LOBs deliver an ultrahigh specific capacity of 13,995 mAh/g at 500 mA g-1, a discharge/charge voltage gap of 0.89 V, and a cycle life up to 523 cycles with a limited capacity of 1000 mAh/g at 500 mA g-1. Impressively, the as-fabricated flexible LOBs with NP-MXene cathode display excellent cycling stability and ability to continuously power LEDs even after bending. Our findings pave the road of heteroatom doped MXenes as next-generation electrodes for high-performance energy storage and conversion systems.

Regulating Lithium Plating and Stripping by Using Vertically Aligned Graphene/CNT Channels Decorated with ZnO Particles.

Lithium (Li) metal is regarded as the ultimate anode material for use in Li batteries due to its high theoretical capacity (3860 mA h g-1 ). However, the Li dendrites that are generated during iterative Li plating/stripping cycles cause poor cycling stability and even present safety risks, and thus severely handicap the commercial utility of Li metal anodes. Herein, we describe a graphene and carbon nanotube (CNT)-based Li host material that features vertically aligned channels with attached ZnO particles (designated ZnO@G-CNT-C) and show that the material effectively regulates Li plating and stripping. ZnO@G-CNT-C is prepared from an aqueous suspension of Zn(OAc)2 , CNTs, and graphene oxide by using ice to template channel growth. ZnO@G-CNT-C was found to be mechanically robust and capable of guiding Li deposition on the inner walls of the channels without the formation of Li dendrites. When used as an electrode, the material exhibits relatively low polarization for Li plating, fast Li-ion diffusion, and high Coulombic efficiency, even over hundreds of Li plating/stripping cycles. Moreover, full cells prepared with ZnO@G-CNT-C as Li host and LiFePO4 as cathode exhibit outstanding performance in terms of specific capacity (155.9 mA h g-1 at 0.5 C), rate performance (91.8 mA h g-1 at 4 C), cycling stability (109.4 mA h g-1 at 0.5 C after 800 cycles). The methodology described can be readily adapted to enable the use of carbon-based electrodes with well-defined channels in a wide range of contemporary applications that pertain to energy storage and delivery.