RESUMEN
The increasing use of nanomaterials in consumer products is expected to lead to environmental contamination sometime soon. As water pollution is a pressing issue that threatens human survival and impedes the promotion of human health, the search for adsorbents for removing newly identified contaminants from water has become a topic of intensive research. The challenges in the recyclability of contaminated water continue to campaign the development of highly reusable catalysts. Although exfoliated 2D MXene sheets have demonstrated the capability towards water purification, a significant challenge for removing some toxic organic molecules remains a challenge due to a need for metal-based catalytic properties owing to their rapid response. In the present study, we demonstrate the formation of hybrid structure AuNPs@MXene (Mo2CTx) during the sensitive detection of Au nanoparticle through MXene sheets without any surface modification, and subsequently its applications as an efficient catalyst for the degradation of 4-nitrophenol (4-NP), methyl orange (MO), and methylene blue (MB). The hybrid structure (AuNPs@MXene) reveals remarkable reusability for up to eight consecutive cycles, with minimal reduction in catalytic efficiency and comparable apparent reaction rate constant (Kapp) values for 4-NP, MB, and MO, compared to other catalysts reported in the literature.
RESUMEN
Nanocomposites and a composite based on poly(butylene adipate-co-terephthalate) (PBAT) were synthesized using commercial copper nanoparticles (Cu-NPs), copper/cuprous oxide nanoparticles (Cu|Cu2O-NPs), and copper sulfate (CuSO4), respectively. The Cu|Cu2O-NPs were synthesized using chemical reduction and characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The synthesis of Cu|Cu2O-NPs yielded a mixture of Cu and Cu2O, with metal Cu having a spherical morphology of approximately 40 nm in diameter and Cu2O with a diameter of 150 nm. To prepare the nanocomposites (NCs) and the composite material (MC), the NPs and the CuSO4 salt were incorporated into the PBAT matrix in concentrations of 1, 3, and 5% p/p via an ex situ method. Fourier transform infrared spectroscopy (FTIR), a tensile test, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and agar diffusion assays were used for structural, thermomechanical, and antimicrobial characterization. Results showed that the reinforcements did not modify the chemical structure of the PBAT and only slightly increased the percentage of crystallization. The mechanical and thermal properties of the PBAT did not change much with the addition of fillers, except for a slight increase in tensile strength and thermal stability, respectively. The agar diffusion antimicrobial assays showed that the NCs and MCs had good inhibitory responses against the nonresistant strains Enterococcus faecalis, Streptococcus mutans, and Staphylococcus aureus. The MCs based on CuSO4 had the highest biocidal effect, even against the resistant bacteria Acinetobacter baumannii.