We demonstrate an optical parametric oscillator (OPO) based on GaAs. The OPO utilizes an all-epitaxially-grown orientation-patterned GaAs crystal that is 0.5 mm thick, 5 mm wide, and 11 mm long, with a domain reversal period of 61.2 microm. Tuning either the near-IR pump wavelength between 1.8 and 2 microm or the temperature of the GaAs crystal allows the mid-IR output to be tuned between 2.28 and 9.14 microm, which is limited only by the spectral range of the OPO mirrors. The pump threshold of the singly resonant OPO is 16 microJ for the 6-ns pump pulses, and the photon conversion slope efficiency reaches 54%. We also show experimentally the possibility of pump-polarization-independent frequency conversion in GaAs.
RESUMEN
Quasi-phase-matched (QPM) GaAs structures, 0.5 mm thick, 10 mm long, and with 61-mum grating periods, were grown by a combination of molecular-beam epitaxy and hydride vapor phase epitaxy. These were characterized by use of mid-IR second-harmonic generation (SHG) with a ZnGeP(2) (ZGP) optical parametric oscillator as a pump source. The SHG efficiencies of QPM GaAs and QPM LiNbO(3) were directly compared, and a ratio of nonlinear coefficients d(14)(GaAs)/d(33) (LiNbO(3))=5.01+/-0.3 was found at 4.1-mum fundamental wavelength. For input pulse energies as low as 50muJ and approximately 60-ns pulse duration, an internal SHG conversion efficiency of 33% was measured in QPM GaAs.
RESUMEN
First-order quasi-phase-matched difference frequency generation of narrowband tunable mid-infrared light is demonstrated in orientation-patterned GaAs. The all-epitaxial orientation-patterned crystal is fabricated by a combination of molecular beam epitaxy and hydride vapor phase epitaxy. Lasers at 1.3 and 1.55 microm were mixed to give an idler output at 8 microm, with power and wavelength tuning consistent with theoretical estimates, indicating excellent material uniformity over the 19-mm-long and 500-microm-thick device.