Carboxymethyl cellulose (CMC) is modified cellulose extracted from oil palm empty fruit bunch (OPEFB) biomass waste that has been prepared through etherification using sodium monochloroacetate (SMCA) in the presence of sodium hydroxide. In this research, CMC hydrogel was prepared using calcium chloride (CaCl2) as the chemical crosslinker. Throughout the optimization process, four important parameters were studied, which were: (1) CMC concentration, (2) CaCl2 concentration, (3) reaction time, and (4) reaction temperature. From the results, the best gel content obtained was 28.11% at 20% (w/v) of CMC with 1% (w/v) of CaCl2 in 24 h reaction at room temperature. Meanwhile, the degree of swelling for CMC hydrogel was 47.34 g/g. All samples were characterized using FT-IR, XRD, TGA, and FESEM to study and compare modification on the OPEFB cellulose. The FT-IR spectrum of CMC hydrogel showed a shift of COO- peaks at 1585 cm-1 and 1413 cm-1, indicating the substitution of Ca2+ into the CMC molecular chains. The XRD diffractogram of CMC hydrogel showed no observation of sharp peaks, which signified an amorphous hydrogel phase. The CrI value also proved the decrement of the crystalline nature of CMC hydrogel. TGA-DTG thermograms showed that the Tmax of CMC hydrogel at 293.33 °C is slightly better in thermal stability compared to CMC. Meanwhile, the FESEM micrograph of CMC hydrogel showed interconnected pores indicating the crosslinkages in CMC hydrogel. CMC hydrogel was successfully synthesized using CaCl2 as a crosslinking agent, and its swelling ability can be used in various applications such as drug delivery systems, industrial effluent, food additives, heavy metal removal, and many more.
RESUMEN
In this study, sago starch was modified in order to enhance its physicochemical properties. Carboxymethylation was used to introduce a carboxymethyl group into a starch compound. The carboxymethyl sago starch (CMSS) was used to prepare smart hydrogel by adding acetic acid into the CMSS powder as the crosslinking agent. The degree of substitution of the CMSS obtained was 0.6410. The optimization was based on the gel content and degree of swelling of the hydrogel. In this research, four parameters were studied in order to optimize the formation of CMSS-acid hydrogel. The parameters were; CMSS concentration, acetic acid concentration, reaction time and reaction temperature. From the data analyzed, 76.69% of optimum gel content was obtained with 33.77 g/g of degree of swelling. Other than that, the swelling properties of CMSS-acid hydrogel in different media such as salt solution, different pH of phosphate buffer saline solution as well as acidic and alkaline solution were also investigated. The results showed that the CMSS-acid hydrogel swelled in both alkaline and salt solution, while in acidic or low pH solution, it tended to shrink and deswell. The production of the hydrogel as a smart material offers a lot of auspicious benefits in the future especially related to swelling behaviour and properties of the hydrogel in different types of media.