RESUMEN
Quasiparticle dynamics of FeSe single crystals revealed by dual-color transient reflectivity measurements (ΔR/R) provides unprecedented information on Fe-based superconductors. The amplitude of the fast component in ΔR/R clearly gives a competing scenario between spin fluctuations and superconductivity. Together with the transport measurements, the relaxation time analysis further exhibits anomalous changes at 90 and 230 K. The former manifests a structure phase transition as well as the associated phonon softening. The latter suggests a previously overlooked phase transition or crossover in FeSe. The electron-phonon coupling constant λ is found to be 0.16, identical to the value of theoretical calculations. Such a small λ demonstrates an unconventional origin of superconductivity in FeSe.
RESUMEN
We investigated the magnetic and ferroelectric properties of c-axis oriented orthorhombic phase HoMnO(3) (o-HMO in Pbnm symmetry setting) thin films grown on Nb-doped SrTiO(3)(001) substrates. The o-HMO films exhibit an antiferromagnetic ordering near 42 K, irrespective of the orientation of the applied field. However, an additional magnetic ordering occurring around 35 K was observed when the field was applied along the c-axis of o-HMO, which was absent when the field was applied in the ab-plane. The magnetocapacitance measured along the c-axis showed that although there is evidence of dielectric constant enhancement when the temperature is below 35 K the expected abrupt change in dielectric constant appears at a much lower temperature and reaches maximum around 13.5 K, indicating that the low-temperature c-axis polarization might be related to the ordering of the Ho(3+) moment. The lattice constant analyses using x-ray diffraction and the observation of a slight magnetization hysteresis suggest that the weak second magnetic transition along the c-axis at 35 K might be more relevant to the strain-induced effect on antiferromagnetism.
RESUMEN
We report on the formation of organized sub-micron YBa(2)Cu(3)O(7) (YBCO) dots induced by irradiating femtosecond laser pulses on YBCO films prepared by pulse laser deposition with fluence in the range of 0.21 approximately 0.53 J/cm(2). The morphology of the YBCO film surface depends strongly on the laser fluences irradiated. At lower laser fluence (approximately 0.21 J/cm(2)) the morphology was pattern of periodic ripples with sub-micrometer spacing. Slightly increasing the laser fluence to 0.26 J/cm(2) changes the pattern into organized sub-micron dots with diameters ranging from 100 nm to 800 nm and height of 150 nm. Further increase of the laser fluence to over 0.32 J/cm(2), however, appeared to result in massive melting and led to irregular morphology. The mechanism and the implications of the current findings will be discussed. Arrays of YBCO sub-micron dots with T(c) = 89.7 K were obtained.