Photocatalysis is a green and cost-effective approach to environmental remediation. While TiO2 is considered one of the benchmark photocatalysts, alternative materials such as Bi2O3 have recently attracted increasing scientific attention as prospective visible light photocatalysts. This study aimed to develop a strategy for Bi2O3 thin film deposition via ultrasonic spray pyrolysis and systematically study process variables for the deposition of ß-Bi2O3 thin films for photocatalytic applications. To achieve the aim, the precursor solution concentration as well as deposition and annealing temperature were optimised. The structural, optical, morphological, chemical and wettability properties of the obtained Bi2O3 thin films were investigated with respect to the effect on the photocatalytic oxidation of 10 ppm methyl orange (MO). The highest photocatalytic activity (48% in 5 h) under UV-A was recorded for the ß-Bi2O3 film deposited using 0.1 M precursor solution at 300 °C and heat-treated for 1 h in air at 350 °C. Deposition at 300 °C resulted in an amorphous film structure, whereas annealing at 350 °C led to the formation of the ß-Bi2O3 phase with the dominant facet orientation (220). These results show the suitability of spray pyrolysis for the deposition of Bi2O3 thin films with promising results for MO dye degradation, expanding the range of suitable photocatalytic materials.
RESUMEN
New semiconductors containing fluorene or fluorenone central fragments along with phosphonic acid anchoring groups were synthesized and investigated as electron transporting materials for possible application in photovoltaic devices. These derivatives demonstrate good thermal stability and suitable electrochemical properties for effective electron transport from perovskite, Sb2S3 and Sb2Se3 absorber layers. Self-assembled fluorene and fluorenone electron-transporting materials have shown improved substrate wettability, indicating bond formation between monolayer-forming compounds and the ITO, TiO2, Sb2S3, or Sb2Se3 surface. Additionally, investigated materials have compatible energetic band alignment and can passivate perovskite interface defects, which makes them interesting candidates for application in the n-i-p structure perovskite solar cell.
RESUMEN
Energy-level alignment is a crucial factor in the performance of thin-film devices, such as organic light-emitting diodes and photovoltaics. One way to adjust these energy levels is through chemical modification of the molecules involved. However, this approach may lead to unintended changes in the optical and/or electrical properties of the compound. An alternative method for energy-level adjustment at the interface is the use of self-assembling monolayers (SAMs). Initially, SAMs with passive spacers were employed, creating a surface dipole moment that altered the work function (WF) of the electrode. However, recent advancements have led to the synthesis of SAM molecules with active spacers. This development necessitates considering not only the modification of the electrode's WF but also the ionization energy (IE) of the molecule itself. To measure both the IE of SAM molecules and their impact on the electrode's WF, a relatively simple method is photo-electric emission spectroscopy. Solar cell performance parameters have a higher correlation coefficient with the ionization energy of SAM molecules with carbazole derivatives as spacers (up to 0.97) than the work function of the modified electrode (up to 0.88). Consequently, SAMs consisting of molecules with active spacers can be viewed as hole transport layers rather than interface layers.
RESUMEN
The rapidly expanding demand for photovoltaics (PVs) requires stable, quick, and easy to manufacture solar cells based on socioeconomically and ecologically viable earth-abundant resources. Sb2S3 has been a potential candidate for solar PVs and the efficiency of planar Sb2S3 thin-film solar cells has witnessed a reasonable rise from 5.77% in 2014 to 8% in 2022. Herein, the aim is to bring new insight into Sb2S3 solar cell research by investigating how the bulk and surface properties of the Sb2S3 absorber and the current-voltage and deep-level defect characteristics of solar cells based on these films are affected by the ultrasonic spray pyrolysis deposition temperature and the molar ratio of thiourea to SbEX in solution. The properties of the Sb2S3 absorber are characterized by bulk- and surface-sensitive methods. Solar cells are characterized by temperature-dependent current-voltage, external quantum efficiency, and deep-level transient spectroscopy measurements. In this paper, the first thin-film solar cells based on a planar Sb2S3 absorber grown from antimony ethyl xanthate (SbEX) by ultrasonic spray pyrolysis in air are demonstrated. Devices based on the Sb2S3 absorber grown at 200 °C, especially from a solution of thiourea and SbEX in a molar ratio of 4.5, perform the best by virtue of suppressed surface oxidation of Sb2S3, favorable band alignment, Sb-vacancy concentration, a continuous film morphology, and a suitable film thickness of 75 nm, achieving up to 4.1% power conversion efficiency, which is the best efficiency to date for planar Sb2S3 solar cells grown from xanthate-based precursors. Our findings highlight the importance of developing synthesis conditions to achieve the best solar cell device performance for an Sb2S3 absorber layer pertaining to the chosen deposition method, experimental setup, and precursors.
RESUMEN
Fluorene-based hole transport materials (HTMs) with terminating thiophene units are explored, for the first time, for antimony sulfide (Sb2S3) solar cells. These HTMs possess largely simplified synthesis processes and high yields compared to the conventional expensive hole conductors making them reasonably economical. The thiophene unit-linked HTMs have been successfully demonstrated in ultrasonic spray-deposited Sb2S3 solar cells resulting in efficiencies in the range of 4.7-4.9% with an average visible transmittance (AVT) of 30-33% (400-800 nm) for the cell stack without metal contact, while the cells fabricated using conventional P3HT have yielded an efficiency of 4.7% with an AVT of 26%. The study puts forward cost-effective and transparent HTMs that avoid a post-coating activation at elevated temperatures like P3HT, devoid of parasitic absorption losses in the visible region and are demonstrated to be well aligned for the band edges of Sb2S3 thereby ascertaining their suitability for Sb2S3 solar cells and are potential candidates for semitransparent applications.
RESUMEN
Recently an efficient dual electroluminescence from monomers and dimers was observed among the structural examples of the emerging emitter class of carbene-metal-amides (CMAs), allowing the preparation of simple design white organic light emitting diodes (wOLEDs). Here we investigate in detail the light emission mechanism in the dimeric species of CMA emitters on the basis of a copper(I) complex TCP bearing thiazoline carbene and 10H-phenothiazine 5,5-dioxide (Ptz) ligands. The X-ray structure for crystals with dimer-only emission was obtained, revealing that emissive aggregates consist of face-to-face stacked molecular pairs with an intermolecular distance of 3.673 Å. The close packing is aided by reduced sterical bulk at the carbene ligand, as well as by a torsional twist between the carbene and amide fragments. Experimental and computational data show that the emission mechanism in aggregates is related to the formation of a persistent dimer, not the excimer. Radiative relaxation proceeds through an intermolecular charge transfer process between the carbene and amide ligands of the neighbouring molecules. In comparison to the monomer, the thermally activated delayed fluorescence (TADF) process in the dimer is characterized with significantly higher energy gaps (ΔEST) between the lowest singlet (S1) and triplet (T1) excited states. At the same time the aggregated species exhibit a significantly increased phosphorescence rate (τ = 12 µs at 10 K temperature) due to the presence of two metal atoms, resulting in a sixfold increase in the spin-orbit coupling (SOC) matrix element in comparison to the monomer.
RESUMEN
Luminescent carbene-metal-amide complexes bearing group 11 metals (Cu, Ag, Au) have recently attracted great attention due to their exceptional emission efficiency and high radiative decay rates (kr). These materials provide a less costly alternative to organic light-emitting diode (OLED) emitters based on more scarce metals, such as Ir and Pt. Herein, a series of eight Cu(I) complexes bearing as yet unexplored 1,3-thiazoline carbenes have been investigated and analyzed with respect to their light emission properties and OLED application. For the first time among the class of copper-based organometallic compounds the formation of efficient electroluminescent excimers is demonstrated. The prevalence of electroluminescence (EL) from either the monomer (bluish green) or the excimer (orange-red) can be adjusted in vacuum-deposited emissive layers by altering the extent of steric encumbrance of the emitter or its concentration. Optimized conditions in terms of the emitter structure and mass fraction allowed a simultaneous EL from the monomer and excimer, which laid the basis for a preparation of a single-emitter white OLED (WOLED) with external quantum efficiency of 16.5% and a maximum luminance of over 40000 cd m-2. Wide overlapping emission bands of the monomer and excimer ensure a device color rendering index (CRI) of above 80. In such a way the prospects of copper complexes as cost-effective materials for lighting devices are demonstrated, offering expense reduction through a cheaper emissive component and a simplified device architecture.
RESUMEN
New push-pull N(9)-alkylated 6-piperidino-2-triazolylpurine and 2-piperidino-6-triazolylpurine derivatives are synthesized, and their optical and optoelectronic properties are comprehensively characterized with experimental and computational methods. The compounds possess intense violet or blue fluorescence with fluorescence quantum yields of up to 91% in solution and 40% in host-free films. Depending on their structural composition, the compounds have ionization energy in the range of 5.25-6.04 eV, electron affinity of 2.18-3.15 eV, and triplet energy of 2.52-2.95 eV. Due to the presence of hole-transporting purine and electron-transporting triazole fragments, compounds exhibit bipolar charge-transportation ability. Despite the favorable emissive properties of the studied push-pull purines, their electroluminescence in thin films is quenched owing to large current densities that are present even at a moderate driving voltage. This marks application directions related to a predominantly charge-transportation functionality as the most suitable for this compound class.
RESUMEN
The through-space charge transfer (CT) process is observed in Cu(I) carbene-metal-amide complexes, where conventional imidazole or imidazoline N-heterocyclic (NHC) carbene fragments act as inert linkers and CT proceeds between a metal-bound carbazole donor and a distantly situated carbene-bound phenylsulfonyl acceptor. The resulting electron transfer gives a rise to efficient thermally activated delayed fluorescence (TADF), characterized with high photoluminescence quantum yields (ΦPL up to 90%) and radiative rates (kr) up to 3.32 × 105 s-1. The TADF process is aided by fast reverse intersystem crossing (rISC) rates of up to 2.56 × 107 s-1. Such emitters can be considered as hybrids of two existing TADF emitter design strategies, combining low singlet-triplet energy gaps (ΔEST) met in all-organic exciplex-like emitters (0.0062-0.0075 eV) and small, but non-negligible spin-orbital coupling (SOC) provided by a Cu atom, like in TADF-active organometallic complexes.
RESUMEN
A group of polyethers containing electroactive pendent 4,7-diarylfluorene chromophores have been prepared by the multi-step synthetic route. Full characterization of their structures has been presented. The polymeric materials represent derivatives of high thermal stability with initial thermal degradation temperatures in a range of 392-397 °C. Glass transition temperatures of the amorphous polymers range from 28 °C to 63 °C and depend on structures of the 4,7-diarylfluorene chromophores. Electron photoemission spectra of thin layers of the electroactive derivatives showed ionization potentials in the range of 5.8-6.0 eV. Hole injecting/transporting properties of the prepared polymeric materials were confirmed during formation of organic light-emitting diodes with tris(quinolin-8-olato)aluminium (Alq3) as a green emitter, which also serves as an electron transporting layer. The device using hole-transporting polymer with electronically isolated 2,7-di(4-biphenyl)fluorene chromophores demonstrated the best overall performance with low turn on voltage of 3 V, high current efficiency exceeding 1.7 cd/A, and with maximum brightness over 200 cd/m2. The organic light-emitting diode (OLED) characteristics were measured in non-optimized test devices. The efficiencies could be further improved by an optimization of device structure, formation conditions, and encapsulation of the devices.
RESUMEN
A series of 1H amorphous tri-phenyl pyridine (HAPPY) dyes have been synthesized from luminescent triphenyl-group-containing 2-methyl-6-styryl-substituted-4H-pyran-4-ylidene derivatives in reactions with benzylamine and investigated for suitability as solution-processable light-emitting medium components in thin films for amplified spontaneous emission (ASE). Conversion of a 4H-pyrane ring into a 1H-pyridine fragment enables aggregation-induced emission enhancement (AIEE) behavior in the target products and slightly increases thermal stability, glass transition temperatures, and ASE efficiency with PLQY up to 15% and ASE thresholds as low as 46 µJ/cm2 in neat spin-cast films, although thermal and photophysical properties are mostly dominated by the incorporated electron acceptors. Continued lasing parameter efficiency parameter improvement experiments revealed that no further optimization of HAPPY dyes by doping in polymer matrixes is required as the amplified spontaneous emission thresholds were lowest in pure neat films due to the AIEE phenomenon.
RESUMEN
Iridium(iii) complexes are the most frequently applied commercialized green and red emitters for organic light emitting diode (OLED) displays. Throughout years a significant research effort has been devoted to modify these compounds, in order to make them suitable for cost-effective solution-processing techniques, such as inkjet printing. To achieve this, the inherent tendency of the complex molecules to form poorly emissive aggregates needs to be suppressed. In many cases this has been achieved by an encapsulation of the iridium(iii) complex core with dendritic structures, composed of either passive or charge-transporting fragments. In order to validate this approach, we acquired three structural analogues of the conventional green emitter Ir(ppy)3, which possess gradually increasing sterical encumberment at the complex surface. Corresponding OLEDs were examined, with three distinctively different active emissive layer compositions in terms of charge transportation characteristics. The results show that in the all scenarios the unmodified Ir(ppy)3 outperforms the compounds with attached bulky groups. The in-device performance of the emitter is directly related to its charge trapping ability, which is being compromised in the presence of dendritic auxiliary substituents.
RESUMEN
The targeted design of lanthanide-based emitters for solution-processed organic light-emitting diodes (OLEDs) resulted in obtaining an NIR OLED with one of the highest efficiencies among ytterbium-based solution-processed OLEDs (30 µW W-1). The design was aimed at the combination of high luminescence efficiency with solubility and charge carrier mobility. The latter was achieved thanks to the introduction of the purposefully selected neutral ligands, which combine electron mobility and the ability to sensitize lanthanide luminescence. Besides, the HOMO and LUMO energies and charge carrier mobility of solution-processed thin films of coordination compounds were measured experimentally for the first time, and novel highly luminescent europium-based materials with PLQYs of up to 80% and purely NIR luminescent ytterbium complexes were obtained.
RESUMEN
Phosphorescent iridium(III) complexes suffer from a strong aggregation quenching, limiting their use in solution-processed or crystalline organic light-emitting diodes. Here we report how an intramolecular stacking between a flexibly bridged bulky aromatic pendant group and the core of nonionic heteroleptic complex can be exploited to minimize the negative effects of this drawback. The stacked conformation provides a rigid sterical shielding of the polar molecular surface, improving photoluminescence quantum yield of the complex both in solution and crystalline state.