Advances in nanotechnology have enabled precise design of catalytic sites for CO2 photoreduction, pushing product selectivity to near unity. However, activity of most nanostructured photocatalysts remains underwhelming due to fast recombination of photogenerated electron-hole pairs and sluggish hole transfer. To address these issues, we construct colloidal CdS nanosheets (NSs) with the large basal planes terminated by S2- atomic layers as intrinsic photocatalysts (CdS-S2- NSs). Experimental investigation reveals that the S2- termination endows ultrathin CdS-S2- NSs with facet-resolved redox-catalytic sites: oxidation occurs on S2--terminated large basal facets and reduction happens on side facets. Such an allocation of redox sites not only promotes spatial separation of photoinduced electrons and holes but also facilitates balanced extraction of holes and electrons by shortening the hole diffusion distance along the (001) direction of the ultrathin NSs. Consequently, the CdS-S2- NSs exhibit superb performance for photocatalytic CO2-to-CO conversion, which was verified by the isotope-labeled experiments to be a record-breaking performance: a CO selectivity of 99%, a CO formation rate of 2.13 mol g-1 h-1, and an effective apparent quantum efficiency of 42.1% under the irradiation (340 to 450 nm) of a solar simulator (AM 1.5G). The breakthrough performance achieved in this work provides novel insights into the precise design of nanostructures for selective and efficient CO2 photoreduction.
RESUMEN
We present facile synthesis of bright CdS/CdSe/CdS@SiO2 nanoparticles with 72% of quantum yields (QYs) retaining ca 80% of the original QYs. The main innovative point is the utilization of the highly luminescent CdS/CdSe/CdS seed/spherical quantum well/shell (SQW) as silica coating seeds. The significance of inorganic semiconductor shell passivation and structure design of quantum dots (QDs) for obtaining bright QD@SiO2 is demonstrated by applying silica encapsulation via reverse microemulsion method to three kinds of QDs with different structure: CdSe core and 2 nm CdS shell (CdSe/CdS-thin); CdSe core and 6 nm CdS shell (CdSe/CdS-thick); and CdS core, CdSe intermediate shell and 5 nm CdS outer shell (CdS/CdSe/CdS-SQW). Silica encapsulation inevitably results in lower photoluminescence quantum yield (PL QY) than pristine QDs due to formation of surface defects. However, the retaining ratio of pristine QY is different in the three silica coated samples; for example, CdSe/CdS-thin/SiO2 shows the lowest retaining ratio (36%) while the retaining ratio of pristine PL QY in CdSe/CdS-thick/SiO2 and SQW/SiO2 is over 80% and SQW/SiO2 shows the highest resulting PL QY. Thick outermost CdS shell isolates the excitons from the defects at surface, making PL QY relatively insensitive to silica encapsulation. The bright SiO2-coated SQW sample shows robustness against harsh conditions, such as acid etching and thermal annealing. The high luminescence and long-term stability highlights the potential of using the SQW/SiO2 nanoparticles in bio-labeling or display applications.