RESUMEN
The magneto-transport properties of single proton-implanted ZnO and of Li(7%)-doped ZnO microwires have been studied. The as-grown microwires were highly insulating and not magnetic. After proton implantation the Li(7%) doped ZnO microwires showed a non-monotonous behavior of the negative magneto-resistance (MR) at temperature above 150 K. This is in contrast to the monotonous NMR observed below 50 K for proton-implanted ZnO. The observed difference in the transport properties of the wires is related to the amount of stable Zn vacancies created at the near surface region by the proton implantation and Li doping. The magnetic field dependence of the resistance might be explained by the formation of a magnetic/non-magnetic heterostructure in the wire after proton implantation.
RESUMEN
We have investigated exchange bias effects in bilayers composed of the antiferromagnetic o-YMnO(3) and ferromagnetic Co thin film by means of SQUID magnetometry, magnetoresistance, anisotropic magnetoresistance and the planar Hall effect. The magnetization and magneto-transport properties show pronounced asymmetries in the field and magnetization axes of the field hysteresis loops. Both exchange bias parameters, the exchange bias field H(E)(T) as well as the magnetization shift M(E)(T), vanish around the Néel temperature T(N) =/~ 45 K. We show that the magnetization shift M(E)(T) is also measured by a shift in the anisotropic magnetoresistance and planar Hall resistance having a similar temperature dependence as the one obtained from magnetization measurements. Because the o-YMnO(3) film is highly insulating, our results demonstrate that the M(E)(T) shift originates at the interface within the ferromagnetic Co layer. To show that the main results obtained are general and not because of some special characteristics of the o-YMO(3) layer, similar measurements were done in Co/CoO micro-wires. The transport and magnetization characterization of the micro-wires supports the main conclusion that these effects are related to the response of the ferromagnetic Co layer at the interface.