The Effect of Magnetoelastic Anisotropy on the Magnetization Processes in Rapidly Quenched Amorphous Nanowires.

In this paper, we report for the first time on the theoretical and experimental investigation of Fe77.5Si7.5B15 amorphous glass-coated nanowires by analyzing samples with the same diameters in both cases. The hysteresis curves, the dependence of the switching field values on nanowire dimensions, and the effect of the magnetoelastic anisotropy on the magnetization processes were analyzed and interpreted to explain the magnetization reversal in highly magnetostrictive amorphous nanowires prepared in cylindrical shape by rapid quenching from the melt. All the measured samples were found to be magnetically bistable, being characterized by rectangular hysteresis loops. The most important feature of the study is the inclusion of the magnetoelastic anisotropy term that originates in the specific production process of these amorphous nanowires. The results show that the switching field decreases when the nanowire diameter increases and this effect is due to the reduction in anisotropy and in the intrinsic mechanical stresses. Moreover, the obtained results reveal the importance of factors such as geometry and magnetoelastic anisotropy for the experimental design of cylindrical amorphous nanowires for multiple applications in miniaturized devices, like micro and nanosensors.

Comparative Study of the Magnetic Behavior of FINEMET Thin Magnetic Wires: Glass-Coated, Glass-Removed, and Cold-Drawn.

In this paper, a comparative investigation of the magnetic behavior and its stress dependence in the case of FINEMET glass-coated, glass-removed, and cold-drawn microwires at low and high frequencies, respectively, is presented. The experimental results show major differences between their magnetic properties depending on the preparation method and microwire diameter. The evolution of the magnetic permeability, coercivity, and magnetoimpedance responses with the applied tensile force was investigated and analyzed in correlation with the stresses induced during preparation, their relief following annealing, and the annealing-induced structural transformations. The coercivity dependence on applied force was found to show the highest sensitivity in the glass-removed microwires, while the magnetic permeability and magnetoimpedance sensitivity to force were found to be higher in the cold-drawn samples. The results of this comparative study will enable an enhanced material selection process for various applications in miniaturized magnetic and stress sensors with increased sensitivity.

Stochastic Magnetization Switching in Rapidly Solidified (Co0.94Fe0.06)72.5Si12.5B15 Amorphous Submicronic Wires.

Submicrometric magnetic amorphous wires are good candidates for future development of miniaturized sensors and magnetic logic applications. Here we report the results of an in-depth investigation of magnetization switching in rapidly solidified nearly zero magnetostrictive (Co0.94Fe0.06)72.5Si12.5B15 amorphous samples with diameters of the actual magnetic wires between 300 and 450 nm. All samples were found to be magnetically bistable, displaying characteristic rectangular hysteresis loops. This shows that magnetization reversal occurs through the depinning and subsequent propagation of a magnetic domain wall, whose velocity depends on the applied field and on the sample dimensions. The results of this study reveal stochastic nonlinear dependencies of both the magnetic switching field and the domain wall velocity on the sample diameter. The analysis of the potential causes, which include nonlinear residual stresses, fluctuations in wire dimensions (metal and glass), and competing magnetic anisotropies of different origins, show that a combination of all three factors could lead to the observed stochastic behavior. Calculated values of the switching field, which consider only changes in the wire dimensions, indicate that such influence alone cannot account for the strong nonlinearities. The results are important for the applications of such ultrathin cylindrical magnetic amorphous wires.