Fluoride-amorphous calcium phosphate and biomimetic nano-hydroxyapatite for enamel remineralization: An in-vitro study of surface microhardness and composition.

AIM: Fluoride-Amorphous Calcium Phosphate and Biomimetic Nano-Hydroxyapatite for Enamel Remineralization; An In-Vitro Study of Surface Microhardness and Composition. MATERIAL AND METHODS: Ninety-six extracted human premolars with sound buccal surface were divided using a randomization computer-generating software into four groups; Group I (control) sound untreated enamel, Group II (demineralized) demineralized to create white spot lesions, Group III (biom-n-HA) demineralized and then treated with biomimetic nanohydroxyapatite cream, and Group IV (F-ACP) demineralized and then treated using Fluoride-Amorphous Calcium Phosphate varnish. Each group was divided into two subgroups; subgroup "A" evaluated for mineral content using energy dispersive x-ray spectroscopy (EDX) and for surface microhardness using the Vickers microhardness test and Subgroup "B" evaluated for white spot lesion depth using a polarized light microscope (PLM). RESULTS: The highest microhardness (VHN) was found in the (F-ACP) group (mean=428.61±54.43) and then in the (Biom-n-HA) group (mean=408.11±70.16) followed by the (Control) group (mean=402.13±53.40) with no significant difference between them and finally in the significantly different (Demineralized) group (mean=256.99±45.83). The weight percentage of Ca (30.29±1.04 and 33.44±1.07) and Ca/P ratio (1.87±0.06 and 2.03±0.05) were significantly different between Group III and Group IV respectively. PLM measurements in Group II (198.83µm), Group III (60.17µm), and Group IV (26.33µm) were significantly different. CONCLUSIONS: Both the (Biom-n-HA) cream and the (F-ACP) varnish showed promising results for enamel remineralization. The increased enamel surface microhardness was consistent with the mineral content and the changes in the birefringence.

Home Oral Care with Biomimetic Hydroxyapatite vs. Conventional Fluoridated Toothpaste for the Remineralization and Desensitizing of White Spot Lesions: Randomized Clinical Trial.

Introduction: Biomimetic hydroxyapatite-based toothpastes have been investigated in recent years for their remineralizing activity on dental surfaces. The aim of the present study was to evaluate the efficacy of toothpaste containing biomimetic hydroxyapatite versus a 1450 pppm fluoride one in promoting the remineralization and desensitization of white spot lesions. Methods: 40 patients were randomly assigned to two different domiciliary oral hygiene treatments: toothpaste containing 1450 ppm of fluoride (control group) and toothpaste containing biomimetic hydroxyapatite (experimental group). Dental sensitivity/pain and dental erosion were assessed at baseline and after 15, 30, and 90 days using the following indexes: Schiff Air Index (SAI), Visual Analogue Scale (VAS), and Basic Erosive Wear Examination (BEWE). Results: Data were submitted for statistical analysis. SAI significantly decreased after 3 months (T3) of treatment only in the Trial group (p < 0.05). VAS values significantly decreased at T2 in the trial group (p < 0.05) with a further significant reduction at T3 (p < 0.05). BEWE scores did not significantly vary during the follow up neither in the trial nor in the control group. Conclusions: The hydroxyapatite-based toothpaste tested caused a reduction of hypersensitivity/pain values higher than conventional fluoride toothpaste.