RESUMO
BACKGROUND: This study is done to evaluate the effect of different reinforcement techniques of overflared root canals with fiber posts on the fracture resistance of endodontically treated anterior teeth. It also introduces a new technique for simultaneous reinforcement and cementation of fiber posts using dual-cured core build-up composite resin. MATERIAL AND METHODS: The crowns of 48 single-rooted maxillary anterior teeth were cut and randomly divided into 4 groups (n=12) based on root reinforcement techniques after root canal treatment and post space preparation: Group 1: self-adhesive resin cement (SARC), Group2: dual-cure composite resin (DCC), Group3: Composite resin reinforcement (CRR), Group 4: Direct anatomical post (DAP). Then a core was made for the roots. The periodontal ligament was simulated using a thin layer of PVC impression material. A universal testing machine applied a compressive force to the lingual surface at an angle of 135 ° and 1 mm/min speed. Data were analyzed using One-Way ANOVA and a post-hoc Tukey test. Fracture patterns were analyzed using the Chi-square test (p<0.05). RESULTS: The difference between the control and DAP group was statistically significant (p=0.01), but there were no significant differences between other groups (p>0.05). Regarding fracture patterns, there were no significant differences between groups. CONCLUSIONS: All reinforcement techniques increased the fracture strength compared to the control group. However, DAP was the only group that had a statistically significant difference. CRR and DCC presented intermediate values without significant differences. Key words:Fiber post, endodontically treated teeth, root canals, reinforcement, fracture strength.
RESUMO
Objectives: The aim of this study was to evaluate the influence of varying dentin and enamel layer thicknesses of two nano-composite resins on color match of composite resins and lithium disilicate dental ceramic. Materials and Methods: Twenty-six specimens of two types of nano-composite resins, Opallis and Vittra, were fabricated using the two-layered technique with different thickness ratios of enamel and dentin composites (A2 shade) with a total thickness of 1.2mm. Thirteen discs of the same shade and thickness of IPS e.max Press LT (low translucency) lithium disilicate dental ceramic were also fabricated. Specimen color was measured with a spectrophotometer. The difference in color (ΔE00) of composite and ceramic specimens, and the translucency parameter (TP) of all specimens were calculated. Data were analyzed using multi-factor ANOVA (P<0.05). Results: The color difference (ΔE00) values of composites and ceramic were not clinically acceptable in any areas of either of the two composites (ΔE00>2.25). But ΔE00 between the two composite resins was in the clinically acceptable range (ΔE00<2.25). The mean TP value of IPS e.max Press was greater than that of Vittra and lower than that of Opallis. Conclusion: In similar thicknesses, composite resins with any enamel/dentin thickness ratio could not successfully simulate the color and translucency of IPS e.max Press LT ceramic.
RESUMO
BACKGROUND: The efficacy of the bond between the restorative materials and the pulp capping materials has an important role in the success of vital pulp therapy. Therefore, the aim of this study was to evaluate the shear bond strength of composite resin and giomer to MTA at different time intervals after mixing of MTA. MATERIAL AND METHODS: Ninety cylindrical MTA samples were prepared and assigned to two groups (n=45) based on the restorative materials used (composite resin or giomer). Each group was subdivided into 3 subgroups (n=15) based on the evaluation intervals (immediately, 2.45 hours and 3 days after mixing MTA). After the bonding procedures, the shear bond strengths of the samples were measured in MPa at a strain rate of 0.5 mm/min. Data were analyzed with repeated-measures ANOVA, post hoc tests and t-test (P<0.05). RESULTS: Bond strength of composite resin was minimum at baseline but it increased significantly 2.45 hours after mixing MTA (P=0.002), with no significant changes in bond strength up to three days (P=0.08). Bond strength of giomer did not exhibit any significant changes from baseline to 2.45 hours after mixing MTA (P=078); however, at 3 days it reached a minimum (P=0.000). In addition, the means of bond strength of composite resin 2.45 hours and 3 days after mixing were significantly higher than those of giomer (P=0.001 and P=0.000, respectively). CONCLUSIONS: Bond strengths of composite resin 2.45 hours and also 3 days after mixing were significantly higher than those of giomer. In addition, the shear bond strength of giomer decreased over time; however, the shear bond strength of composite resin increased. Key words:Composite resin, Giomer, Shear bond strength, Vital pulp therapy.
RESUMO
BACKGROUND: Considering the probability of chemical and enzymatic reactions between matrix metalloproteinases (MMPs) in the dentin structure and their specific inhibitors, the aim of the present study was to evaluate the effect of different concentrations of specific inhibitor of MMPs (galardin) on the shear bond strength of self-adhesive resin cements to dentin. MATERIAL AND METHODS: Forty-eight sound human premolars were mounted in self-cured acrylic resin after removal of the enamel on the buccal and lingual surfaces. The dentin surfaces achieved were polished and prepared with 600-grit silicon carbide paper. The samples were divided into 3 groups (n=16) based on the concentration of galardin used (with no galardin, galardin at a high concentration and galardin at a low concentration). In addition, 96 composite resin blocks, measuring 3 mm in height and diameter, were prepared. The composite resin blocks were bonded to the buccal and lingual surface dentin with Rely-X Unicem (RXC) and Speed CEM (SPC) self-adhesive resin cements, respectively, according to manufacturers' instructions. After 24 hours of storage in distilled water at 37°C, the shear bond strength values were determined in MPa and fracture modes were evaluated under a stereomicroscope. Data were analyzed with two-way ANOVA and post-hoc Bonferroni test (α=0.05). RESULTS: The shear bond strength of galardin at high concentration was significantly higher than that in the control group and galardin at a low concentrations (P<0.001). In addition, galardin at a low concentration exhibited higher shear bond strength compared to the control group (P=0.005). Furthermore, higher shear bond strength values were reported with the use of RXC compared to SPC (P<0.001). CONCLUSIONS: Irrigation with galardin increased the shear bond strength of self-adhesive resin cements to dentin and this increase had a direct relationship with the concentration of galardin in the solution. Key words:N-(2(R)-2-(hydroxamidocarbonylmethyl)-4-methylpentanoyl)-L-tryptophan methylamide, Matrix metalloproteinase inhibitors, Dentin, Extracellular matrix, Luting agents, Dental Bonding.
RESUMO
Background and aims. Present study was designed to compare the bonding strength of resin-modified glass ionomer (RMGI) and composite resin to mineral trioxide aggregate (MTA), MTA mixed with Na2HPO4 (NAMTA), and calcium-enriched mixture (CEM). Materials and methods. Thirty specimens of each CEM, NAMTA, and MTA were prepared. Composite and RMGI restorations were then placed on the samples (15 samples in six subgroups). Shear bond strength was assessed using universal testing machine. Data were analyzed with two-way ANOVA and post-hoc Tukey test. To compare the bond strength in subgroups, one-away ANOVA was applied. Significance level was set at P < 0.05. Results. Bond strength was significantly higher to composite samples compared to RMGI samples (p<0.001). The difference in bond strength of composite samples between MTA and CEM subgroups (P=0.026) as well as MTA and NAMTA subgroups (P= 0.019) was significant, but the difference between NAMTA and CEM subgroups (P=0.56) was not significant. The differences in bond strength in subgroups of RMGI group were not significant (P>0.05). Conclusion. Regarding shear bond strength to the tested substrates, composite was shown to be superior to RMGI. The bond of resin composite to MTA was weaker than that to CEM and NAMTA.
RESUMO
The weak link in the adhesive luting of fiber posts to root canal dentin is at the cement-dentin interface. The aim of the present study was to evaluate the effect of Er,Cr:YSGG laser irradiation on push-out bond strength of fiber posts cemented to root canal dentin using a self-adhesive cement. A total of 30 sound human maxillary central incisors were equally divided into two groups after root canal treatment, decoronation and preparation of the post space. Teeth of group 1 were treated with the Er,Cr:YSGG laser, and teeth of group 2 (control) received no laser treatment. After cementation of fiber posts with Maxcem self-adhesive cement, 3-mm cervical, middle and apical sections were prepared from the roots. Then a push-out test was performed using a universal testing machine at a strain rate of 0.5 mm/min. Data were analyzed using two-way ANOVA and the Bonferroni test. Statistical significance was defined as P < 0.05. There was a significant difference in the mean bond strength values between groups 1 and 2 (P = 0.001), but there were no significant differences between the various root parts (P = 0.14). In addition, the cumulative effects of dentin treatment type and various root parts were not statistically significant (P = 0.41). The mean bond strength in the laser group was significantly higher than in the control group (P = 0.001, post hoc Bonferroni test).The failure mode was evaluated under a stereomicroscope at × 20 magnification.