Study of all-group-IV SiGeSn mid-IR lasers with dual wavelength emission.

Direct band gap GeSn alloys have recently emerged as promising lasing source materials for monolithic integration on Si substrate. In this work, optically pumped mid-infrared GeSn lasers were studied with the observation of dual-wavelength lasing at 2187 nm and 2460 nm. Two simultaneous lasing regions include a GeSn buffer layer (bulk) and a SiGeSn/GeSn multiple quantum well structure that were grown seamlessly using a chemical vapor deposition reactor. The onset of dual lasing occurs at 420 kW/cm2. The wider bandgap SiGeSn partitioning barrier enables the independent operation of two gain regions. While the better performance device in terms of lower threshold may be obtained by using two MQW regions design, the preliminary results and discussions in this work paves a way towards all-group-IV dual wavelength lasers monolithically integrated on Si substrate.

Investigation of the cap layer for improved GeSn multiple quantum well laser performance.

The study of all-group-IV SiGeSn lasers has opened a new avenue to Si-based light sources. SiGeSn heterostructure and quantum well lasers have been successfully demonstrated in the past few years. It has been reported that, for multiple quantum well lasers, the optical confinement factor plays an important role in the net modal gain. In previous studies, adding a cap layer was proposed to increase the optical mode overlap with the active region and thereby improve the optical confinement factor of Fabry-Perot cavity lasers. In this work, SiGeSn/GeSn multiple quantum well (4-well) devices with various cap layer thicknesses, i.e., 0 (no cap), 190, 250, and 290 nm, are grown using a chemical vapor deposition reactor and characterized via optical pumping. While no-cap and thinner-cap devices only show spontaneous emission, the two thicker-cap devices exhibit lasing up to 77 K, with an emission peak at 2440 nm and a threshold of 214 kW/cm2 (250 nm cap device). The clear trend in device performance disclosed in this work provides guidance in device design for electrically injected SiGeSn quantum well lasers.

Growth of Pseudomorphic GeSn at Low Pressure with Sn Composition of 16.7.

Group-IV alloy GeSn holds great promise for the high-performance optoelectronic devices that can be monolithically integrated on Si for near- and mid-infrared applications. Growth of GeSn using chemical vapor deposition technique with various Sn and Ge precursors has been investigated worldwide. To achieve relatively high Sn incorporation, the use of higher pressure and/or higher order Ge hydrides precursors were reported. In this work, we successfully demonstrated the growth of high-quality GeSn with Sn composition of 16.7% at low pressure of 12 Torr. The alloy was grown using the commercially available GeH4 and SnCl4 precursors via a chemical vapor deposition reactor. Material and optical characterizations were performed to confirm the Sn incorporation and to study the optical properties. The demonstrated growth results reveal a low-pressure growth window to achieve high-quality and high Sn alloys for future device applications.

Investigation of SiGeSn/GeSn/SiGeSn single quantum well with enhanced well emission.

In this work, a SiGeSn/GeSn/SiGeSn single quantum well was grown and characterized. The sample has a thicker GeSn well of 22nm compared to a previously reported 9nm well configuration. The thicker well leads to: (i) lowered ground energy level in Γ valley offering more bandgap directness; (ii) increased carrier density in the well; and (iii) improved carrier collection due to increased barrier height. As a result, significantly enhanced emission from the quantum well was observed. The strong photoluminescence (PL) signal allows for the estimation of quantum efficiency (QE), which was unattainable in previous studies. Using pumping-power-dependent PL spectra at 20K, the peak spontaneous QE and external QE were measured as 37.9% and 1.45%, respectively.

Study of direct bandgap type-I GeSn/GeSn double quantum well with improved carrier confinement.

The GeSn-based quantum wells (QWs) have been investigated recently for the development of efficient GeSn emitters. Although our previous study indicated that the direct bandgap well with type-I band alignment was achieved, the demonstrated QW still has insufficient carrier confinement. In this work, we report the systematic study of light emission from the Ge0.91Sn0.09/Ge0.85Sn0.15/Ge0.91Sn0.09 double QW structure. Two double QW samples, with the thicknesses of Ge0.85Sn0.15 well of 6 and 19 nm, were investigated. Band structure calculations revealed that both samples feature type-I band alignment. Compared with our previous study, by increasing the Sn composition in GeSn barrier and well, the QW layer featured increased energy separation between the indirect and direct bandgaps towards a better direct gap semiconductor. Moreover, the thicker well sample exhibited improved carrier confinement compared to the thinner well sample due to lowered first quantized energy level in the Γ valley. To identify the optical transition characteristics, photoluminescence (PL) study using three pump lasers with different penetration depths and photon energies was performed. The PL spectra confirmed the direct bandgap well feature and the improved carrier confinement, as significantly enhanced QW emission from the thicker well sample was observed.