New pectin derivatives with antimicrobial and emulsification properties via complexation with metal-terpyridines.

Pectin is widely used in food and pharmaceutical industries. However, due to its polysaccharide nature it lacks antimicrobial activity. In the current work, new pectin derivatives with interesting optical and antimicrobial properties were prepared via supramolecular chemistry utilizing Fe- or Cu-terpyridine (Tpy-Fe and Tpy-Cu) motifs. To proof derivatization of pectin, ultraviolet-visible spectroscopy (UV-Vis) and Fourier Transform infrared (FTIR) were used. In addition, the prepared pectin derivatives retained the known emulsification activity of the non-modified sugar beet pectin as seen from the particle size analysis of oil-in-water emulsions. The prepared derivatives showed antibacterial activity toward selected Gram-positive and Gram-negative bacteria. In addition, cytotoxicity test showed that the Tpy-Fe-pectin derivative was non-toxic to cells of human hepatocarcinoma, breast adenocarcinoma MCF7, and colorectal carcinoma cells at concentrations up to 100 µg/ml, while Tpy-Cu-pectin had moderate toxicity toward the aforementioned cells at the same concentration levels. The prepared derivatives could have potential applications in emulsions with antibacterial activity.

Water purification ultrafiltration membranes using nanofibers from unbleached and bleached rice straw.

There has been an increasing interest in recent years in isolating cellulose nanofibers from unbleached cellulose pulps for economic, environmental, and functional reasons. In the current work, cellulose nanofibers isolated from high-lignin unbleached neutral sulfite pulp were compared to those isolated from bleached rice straw pulp in making thin-film ultrafiltration membranes by vacuum filtration on hardened filter paper. The prepared membranes were characterized in terms of their microscopic structure, hydrophilicity, pure water flux, protein fouling, and ability to remove lime nanoparticles and purify papermaking wastewater effluent. Using cellulose nanofibers isolated from unbleached pulp facilitated the formation of a thin-film membrane (with a shorter filtration time for thin-film formation) and resulted in higher water flux than that obtained using nanofibers isolated from bleached fibers, without sacrificing its ability to remove the different pollutants.

Effect of Unbleached Rice Straw Cellulose Nanofibers on the Properties of Polysulfone Membranes.

In addition to their lower cost and more environmentally friendly nature, cellulose nanofibers isolated from unbleached pulps offer different surface properties and functionality than those isolated from bleached pulps. At the same time, nanofibers isolated from unbleached pulps keep interesting properties such as hydrophilicity and mechanical strength, close to those isolated from bleached pulps. In the current work, rice straw nanofibers (RSNF) isolated from unbleached neutral sulfite pulp (lignin content 14%) were used with polysulfone (PSF) polymer to make membrane via phase inversion. The effect of RSNF on microstructure, porosity, hydrophilicity, mechanical properties, water flux, and fouling of PSF membranes was studied. In addition, the prepared membranes were tested to remove lime nanoparticles, an example of medium-size nanoparticles. The results showed that using RSNF at loadings from 0.5 to 2 wt.% can significantly increase hydrophilicity, porosity, water flux, and antifouling properties of PSF. RSNF also brought about an increase in rejection of lime nanoparticles (up to 98% rejection) from their aqueous suspension, and at the same time, with increasing flux across the membranes. Tensile strength of the membranes improved by ~29% with addition of RSNF and the maximum improvement was obtained on using 0.5% of RSNF, while Young's modulus improved by ~40% at the same RSNF loading. As compared to previous published results on using cellulose nanofibers isolated from bleached pulps, the obtained results in the current work showed potential application of nanofibers isolated from unbleached pulps for improving important properties of PSF membranes, such as hydrophilicity, water flux, rejection, and antifouling properties.