RESUMO
Probing of the free surface ferroelectric properties of thin polar films can be achieved either by estimating the band bending variance under the top-most layer or by studying the extent of the extrinsic charge accumulated outside the surface. Photoemitted or incoming low-energy electrons can be used to characterize locally both properties in a spectromicroscopic approach. Thin ferroelectric lead zirco-titanate (PZT) is investigated by combining low energy/mirror electron microscopy (LEEM/MEM) with photoemission electron microscopy (PEEM) and high-resolution photoelectron spectroscopy (XPS). Significant extrinsic negative compensation charge is proven to accumulate on the surface of the outward polarized thin film, indicated by high MEM-LEEM transition values, up to 15.3 eV, and is correlated with the surface electrostatic potential, which can be partially screened either by electrons interacting with the sample or by soft X-rays through the ejection of secondary electrons and generation of positive charge under the surface. A radiation-induced surface charge compensation effect is observed. The study indicates that air-exposed high quality ferroelectric thin films show large negative surface potentials, determined locally on the surface, which are nevertheless sensitive to beam damage and molecular desorption. These values represent a confirmation of previously estimated surface potential energy values determined from the LEED data on clean surfaces.
RESUMO
The stability of thin films of lead zirco-titanate (PZT) under intense soft X-ray beams is investigated by time-resolved photoelectron spectromicroscopy with a lateral resolution below 1 micrometer. Surface dissociation is observed when samples are irradiated with intense (5 × 1023 photons per s per m2) soft X-rays, with promotion of reduced lead on the surface. On areas exhibiting outwards polarization (P(+)), the reduced lead is formed at the expense of P(+)-PZT. On areas presenting co-existing P(+) states with areas without out-of-plane polarization (P(0)), the reduced lead is formed at the expense of the P(0)-PZT component, while the P(+)-PZT remains constant. The main dissociation mechanism was found to be triggered by 'hot' electrons in the conduction band, with energies exceeding the surface dissociation energies. Dissociation occurs basically when the electron affinity is larger than the dissociation energy of PbO (for P(+) areas) or PbO- (for P(0) areas). Such mechanisms may be adapted for dissociation of other molecules on surfaces of ferroelectric thin films or for quantifying the stability of ferroelectric surfaces interacting with other radiation, with applications in the fields of photocatalysis or photovoltaic devices.