RESUMO
Lead halide perovskite nanocrystals (NCs) are emerging as optically active materials for solution-processed optoelectronic devices. Despite the technological relevance of tracing rational guidelines for optimizing their performances and stability beyond their intrinsic resilience to structural imperfections, no in-depth study of the role of selective carrier trapping and environmental conditions on their exciton dynamics has been reported to date. Here we conduct spectro-electrochemical (SEC) experiments, side-by-side to oxygen sensing measurements on CsPbBr3 NCs for the first time. We show that the application of EC potentials controls the emission intensity by altering the occupancy of defect states without degrading the NCs. Reductive potentials lead to strong (60%) emission quenching by trapping of photogenerated holes, whereas the concomitant suppression of electron trapping is nearly inconsequential to the emission efficiency. Consistently, oxidizing conditions result in minor (5%) brightening due to suppressed hole trapping, confirming that electron traps play a minor role in nonradiative decay. This behavior is rationalized through a model that links the occupancy of trap sites with the position of the NC Fermi level controlled by the EC potential. Photoluminescence measurements in controlled atmosphere reveal strong quenching by collisional interactions with O2, which is in contrast to the photobrightening effect observed in films and single crystals. This indicates that O2 acts as a scavenger of photoexcited electrons without mediation by structural defects and, together with the asymmetrical SEC response, suggests that electron-rich defects are likely less abundant in nanostructured perovskites than in the bulk, leading to an emission response dominated by direct interaction with the environment.
RESUMO
We report chemical routes for the synthesis of both nanocrystals and bulk crystals of methylammonium (MA) lead halide perovskites employing N-methylformamide (NMF) as a source of MA ions. Colloidal nanocrystals were prepared by a transamidation reaction between NMF and an alkyl amine (oleylamine). The nanocrystals showed photoluminescence quantum yields reaching 74% for MAPbBr3 and 60% for MAPbI3. Bulk crystals were grown at room temperature, with no need for an antisolvent, by the acid hydrolysis of NMF. Important advantages of using NMF instead of MA salts are that the syntheses involve fewer steps and less toxic and less expensive chemicals.
RESUMO
We demonstrate that, via controlled anion exchange reactions using a range of different halide precursors, we can finely tune the chemical composition and the optical properties of presynthesized colloidal cesium lead halide perovskite nanocrystals (NCs), from green emitting CsPbBr3 to bright emitters in any other region of the visible spectrum, and back, by displacement of Cl(-) or I(-) ions and reinsertion of Br(-) ions. This approach gives access to perovskite semiconductor NCs with both structural and optical qualities comparable to those of directly synthesized NCs. We also show that anion exchange is a dynamic process that takes place in solution between NCs. Therefore, by mixing solutions containing perovskite NCs emitting in different spectral ranges (due to different halide compositions) their mutual fast exchange dynamics leads to homogenization in their composition, resulting in NCs emitting in a narrow spectral region that is intermediate between those of the parent nanoparticles.