J Colloid Interface Sci ; 369(1): 470-6, 2012 Mar 01.
Artigo em Inglês | MEDLINE | ID: mdl-22200328

RESUMO

Inorganic/organic hybrids were obtained by the sol-gel type organic modification reaction of Laponite sidewalls with poly(ethylene glycol) (PEG) bearing alkoxysiloxy terminal functionality. By casting an aqueous dispersion of the hybrid, the flexible and transparent hybrid films were obtained. Regardless of the inorganic/organic component ratio, the hybrid film had the ordered structure of Laponite in-plane flat arrays. The mechanical strength of hybrid films was drastically improved by the presence of cross-linking among alkoxysilyl functionalities of PEG terminals and the absence of PEG crystallines. Hybrid films, especially those that consisted of PEG with short chain, showed good mechanical properties that originate from quasi-homogeneous dispersion of components due to anchoring of PEG terminal to Laponite sidewall and interaction of PEG to Laponite surface.

2.
Langmuir ; 26(15): 12493-5, 2010 Aug 03.
Artigo em Inglês | MEDLINE | ID: mdl-20586428

RESUMO

A flexible, transparent nanocomposite (NC) film with 57 wt % inorganic components was obtained by the simple casting of a solution of Laponite and modified organic molecules through a sol-gel reaction. The NC film has solvent resistance and a disco-nematic liquid-crystalline-like structure of Laponite that originates from the cross linking of Laponite by silanol agents and the large amount of Laponite in the film.