RESUMO
The aim of the present study was to evaluate the effect of the surface treatments on flexural strengths and flexural modulus of glass-fibre-reinforced composite (GFRC) posts. Sixty-three posts were randomly divided into 9 groups (n = 7), and various surface treatments were performed. The control group was left untreated. Other groups were treated with 9% hydrofluoric acid, sandblasting with 120 µm Al2 O3 particles and Er,Cr:YSGG laser irradiation with different powers (1 W, 2 W, 3 W, 4 W, 5 W and 6 W). The samples were subjected to 3-point bending test, and data were calculated. Statistical analysis was performed. The flexural strengths of fibre posts treated with sandblasting, hydrofluoric acid, 1 W and 2 W laser were statistically similar with control group (P > 0.01). However, the flexural strength of fibre posts treated with 3 W, 4 W, 5 W and 6 W laser was statistically lower than control group (P < 0.01). High laser irradiations cause melting on the post surface and breaks in fibrils.