Oxygen vacancy-rich high-pressure rocksalt phase of zinc oxide for enhanced photocatalytic hydrogen evolution.

The generation of hydrogen as a clean energy carrier by photocatalysis, as a zero-emission technology, is of significant scientific and industrial interest. However, the main drawback of photocatalytic hydrogen generation from water splitting is its low efficiency compared to traditional chemical or electrochemical methods. Zinc oxide (ZnO) with the wurtzite phase is one of the most investigated photocatalysts for hydrogen production, but its activity still needs to be improved. In this study, an oxygen-deficient high-pressure ZnO rocksalt phase is stabilized using a high-pressure torsion (HPT) method, and the product is used for photocatalysis under ambient pressure. The simultaneous introduction of oxygen vacancies and the rocksalt phase effectively improved photocatalytic hydrogen production to levels comparable to benchmark P25 TiO2, due to improving light absorbance and providing active sites for photocatalysis without any negative effect on electron-hole recombination. These results confirm the high potential of high-pressure phases for photocatalytic hydrogen generation.

Catalytic Behavior of K-doped Fe/MgO Catalysts for Ammonia Synthesis Under Mild Reaction Conditions.

An important part of realizing a carbon-neutral society using ammonia will be the development of an inexpensive yet efficient catalyst for ammonia synthesis under mild reaction conditions (<400 °C, <10 MPa). Here, we report Fe/K(3)/MgO, fabricated via an impregnation method, as a highly active catalyst for ammonia synthesis under mild reaction conditions (350 °C, 1.0 MPa). At the mentioned conditions, the activity of Fe/K(3)/MgO (17.5 mmol h-1 gcat -1 ) was greater than that of a commercial fused iron catalyst (8.6 mmol h-1 gcat -1 ) currently used in the Haber-Bosch process. K doping was found to increase the ratio of Fe0 on the surface and turnover frequency of Fe in our Fe/K(3)/MgO catalyst. In addition, increasing the pressure to 3.0 MPa at the same temperature led to a significant improvement of the ammonia synthesis rate to 29.6 mmol h-1 gcat -1 , which was higher than that of two more expensive, benchmark Ru-based catalysts, which are also potential alternative catalysts. A kinetics analysis revealed that the addition of K enhanced the ammonia synthesis activity at ≥300 °C by changing the main adsorbed species from NH to N which can accelerate dissociative adsorption of nitrogen as the rate limiting step in ammonia synthesis.

Advanced Photocatalysts for CO2 Conversion by Severe Plastic Deformation (SPD).

Excessive CO2 emission from fossil fuel usage has resulted in global warming and environmental crises. To solve this problem, the photocatalytic conversion of CO2 to CO or useful components is a new strategy that has received significant attention. The main challenge in this regard is exploring photocatalysts with high efficiency for CO2 photoreduction. Severe plastic deformation (SPD) through the high-pressure torsion (HPT) process has been effectively used in recent years to develop novel active catalysts for CO2 conversion. These active photocatalysts have been designed based on four main strategies: (i) oxygen vacancy and strain engineering, (ii) stabilization of high-pressure phases, (iii) synthesis of defective high-entropy oxides, and (iv) synthesis of low-bandgap high-entropy oxynitrides. These strategies can enhance the photocatalytic efficiency compared with conventional and benchmark photocatalysts by improving CO2 adsorption, increasing light absorbance, aligning the band structure, narrowing the bandgap, accelerating the charge carrier migration, suppressing the recombination rate of electrons and holes, and providing active sites for photocatalytic reactions. This article reviews recent progress in the application of SPD to develop functional ceramics for photocatalytic CO2 conversion.