Effect of simulated gastric acid exposure on the hardness, topographic, and colorimetric properties of machinable and pressable zirconia-reinforced lithium silicate glass-ceramics.

STATEMENT OF PROBLEM: The effects of gastric acid on the hardness, topographic, and colorimetric properties of zirconia-reinforced lithium silicate glass-ceramics (ZLSs) for dental restorations remain unknown. PURPOSE: The purpose of this in vitro study was to investigate the effect of simulated gastric acid exposure on the microhardness, surface roughness, color stability, and relative translucency of ZLSs. MATERIAL AND METHODS: Two pressable ZLSs (VITA AMBRIA, VA and Celtra Press, CP) and 2 machinable ZLSs (VITA Suprinity, VS and Celtra Duo, CD)(n=64) were randomly allocated to artificial saliva (control) or gastric juice immersion groups simulating 10 and 20 years of clinical exposure. Microhardness (Hv) was measured with a Vickers hardness device, and surface roughness (Sa) was recorded with an optical profilometer. The color stability (ΔE00) and relative translucency parameter (RTP) were measured with a spectrophotometer. Data for Hv, Sa, and RTP were analyzed by repeated 2-way ANOVA, and data for ΔE00 were analyzed by 2-way ANOVA. Post hoc comparisons were obtained from Tukey HSD and Student t tests (α=.05). RESULTS: Machinable ZLSs exhibited greater Hv after the simulated gastric acid challenge than pressable ZLSs. Sa was significantly impacted by material type (P=.001), storage media (P=.050), and their interaction (P<.001). ΔE00 was significantly affected by the type of simulated aging media (P<.001). After 20 years of simulated gastric acid aging, all ZLS materials surpassed the ΔE00 perceptibility threshold but did not exceed the ΔE00 acceptability threshold. VS displayed significantly lower RTP than other ZLS materials at all time points (P<.001). CONCLUSIONS: The topographic and colorimetric characteristics of ZLS were significantly altered by exposure to simulated gastric acid.

Staining and bleaching susceptibility of zirconia-reinforced lithium silicate glass-ceramics with different thicknesses, translucencies, and fabrication methods.

STATEMENT OF PROBLEM: The influence of different thicknesses, translucencies, and fabrication methods on the spectrophotometric and topographical properties of zirconia-reinforced lithium silicate glass-ceramics (ZLSs) for dental restorations remains unclear. PURPOSE: The purpose of this in vitro study was to investigate the effect of thicknesses, translucencies, and fabrication methods on the color stability, translucency parameter, opalescence parameter, whiteness stability, transmitted irradiance, light transmittance, opacity, gloss, and roughness of ZLSs exposed to coffee staining and bleaching treatments. MATERIAL AND METHODS: Two pressable ZLSs (VITA AMBRIA, VA and Celtra Press, CP) and 2 machinable ZLSs (VITA Suprinity, VS and Celtra Duo, CD) were examined at high translucency (HT) and low translucency (LT) levels in 2 thicknesses (n=160). The specimens were evaluated at baseline, after coffee staining, and after bleaching. The color stability (ΔE2000), translucency parameter (TP), opalescence parameter (OP), whiteness index (WID), and whiteness stability (ΔWID) were measured with a spectrophotometer. Transmitted irradiance (It), light transmission (T), and opacity (O) were obtained from a light-polymerizing unit and a polymerization light collection device. Roughness stability (ΔSa%) was determined with an optical profilometer, and gloss stability (ΔGU%) was recorded with a gloss meter. Data of ΔCIE2000, ΔWID, ΔSa%, and ΔGU% were analyzed by 4-way ANOVA, and data of the TP, OP, WID, It, T, and O were analyzed by repeated 4-way ANOVA (α=.05). RESULTS: VS-HT exceeded the ΔCIE2000 acceptability threshold after coffee staining and bleaching protocols. Pressable ZLSs exhibited greater color stability than machinable ZLSs. The 1-mm-thick VA, CP, and CD materials exceeded the ΔWID perceptibility threshold after bleaching. The highest TP and OP was displayed by the 1-mm-thick CP after bleaching. ΔGU increased after water storage and decreased after coffee staining and bleaching. ΔSa% significantly increased after bleaching (P<.05). CONCLUSIONS: The color stability and other spectrophotometric properties of ZLSs depended on material thickness. The effects of ZLS fabrication methods and translucency levels on their measured properties were inconsistent. Subjecting 1-mm-thick ZLS materials to acidic media adversely impacted their stainability and surface texture.

Effect of repeated firing on the topographical, optical, and mechanical properties of fully crystallized lithium silicate-based ceramics.

STATEMENT OF PROBLEM: The influence of different firing protocols on the topographical, optical, and mechanical properties of fully crystallized computer-aided design and computer-aided manufacturing (CAD-CAM) lithium silicate-based glass-ceramics (LSCs) for dental restorations remains unclear. PURPOSE: The purpose of this in vitro study was to investigate the effect of different firing regimens on the surface roughness, gloss, Martens hardness, indentation modulus, biaxial flexural strength, and crystalline structure of fully crystallized CAD-CAM LSCs and the effect of their interposition on the irradiance of a light-polymerization unit. MATERIAL AND METHODS: Three fully crystallized CAD-CAM LSC blocks were evaluated (N=150): lithium disilicate (Initial LiSi Blocks; LS), zirconia-reinforced silicate (Celtra Duo; CD), and lithium aluminum disilicate (CEREC Tessera; CT). Specimens were allocated to 5 subgroups according to their firing protocol. LSC roughness (Sa) was measured with an optical profilometer, and gloss (GU) was detected with a gloss meter. Martens hardness (HM) and indentation modulus (EIT) data were obtained from a hardness testing machine. The irradiance of a light-polymerization unit and transmittance of LSCs were measured with an instrument (Managing Accurate Resin Curing-Light Collector; BlueLight analytics, Inc) subsequent to ceramic interposition. Crystalline phases were analyzed by X-ray diffraction, and biaxial flexural strength (σ) was determined by the ball-on-3-ball method in a universal testing machine followed by Weibull analysis to calculate characteristic strength (σ0) and Weibull modulus (m). Two-way ANOVA and Tukey HSD post hoc tests (α=.05) were used to analyze the data. RESULTS: Statistically significant differences were found among different treatment groups based on Sa, GU, HM, and EIT values (P<.001). Delivered irradiance was significantly reduced following CT (P<.01) and glazed LSC (P<.005) interposition. CD displayed highest biaxial flexural strength and reliability after 1 firing cycle (σ=568.2 MPa, m=16.8) CONCLUSIONS: The type of material and firing regimens had a significant effect on the topographical, optical, and mechanical properties of fully crystallized CAD-CAM LSCs. Glazing significantly reduced delivered irradiance, Martens hardness, and biaxial flexural strength.

Effect of surface treatments on optical, topographical and mechanical properties of CAD/CAM reinforced lithium silicate glass ceramics.

OBJECTIVES: To investigate the effect of different surface treatments on optical, topographical and mechanical properties of CAD/CAM lithium silicate-based glass ceramics (LSC's) and their combined effect on the output of a light curing unit (LCU). METHODS: Four CAD/CAM LSC's were investigated: Lithium Disilicate (Emax CAD; EC), Zirconia-reinforced silicates (Vita Suprinity; VS and Celtra Duo;CD) and Lithium Aluminum Disilicate (CEREC Tessera; CT). Ceramic specimens (n = 240) were divided into six subgroups according to their surface treatment: (a) Control, (b) Hydrofluoric acid (HF) 5%, (c) HF 5% + Neutralizing agent (N), (d) HF 9%, (e) HF 9% +N and (f) Self-etching ceramic primer (SEP). Irradiance, power and radiant exposure of a LCU were measured with MARC-LC following ceramic specimen interposition. Direct light transmission (T%) and absorbance (Abs%) of the specimens were measured with UV-Vis spectrophotometry. Roughness (Sa, Sq) and wettability (θ°) were measured with optical profilometry and sessile drop profile analysis, respectively. Biaxial flexural strength (σ) of the ceramic specimens was measured by the ball-on-three-balls method and ceramic specimens were examined microscopically. Statistical analyses was performed by two-way ANOVA followed by post hoc multiple comparisons (α = 0.05). RESULTS: Acid neutralization decreased T% and increased Abs% in all LSC's and highest T% was exhibited with VS. Neutralized EC, VS and CD displayed higher Sa in HF9, while neutralized CT displayed higher Sa in HF5. Self-etch primer significantly reduced θ° (p < 0.001). σ was observed in the followed ascending order: HF9 +N < HF9 < HF5 +N < HF5 < SEP < Control for all LSC's. SIGNIFICANCE: Optical, topographical and mechanical properties of the CAD/CAM ceramic blocks were strongly dependent on the type of surface treatment. Results of neutralization post-etching indicate promising potential for future investigations.