RESUMO
Photocatalytic materials have received great interest due to their capability for remediating environmental pollution especially water pollution. However, the scalable application of the current photocatalytic materials is still limited by their poor visible-light absorption and low separation efficiency of charge carriers. Here, we report in-situ sunlight-driven tuning of photo-induced electron-hole generation and separation rates in bismuth oxychlorobromide (BiOCl0.8Br0.2) nanoflowers. It shows photochromic response under 10-minute natural sunlight irradiation changing color from white to black. The characterization reveals the presence of hydroxyl groups on the surface of the pristine BiOCl0.8Br0.2 nanoflowers and abundant oxygen vacancies for the sunlight-irradiated BiOCl0.8Br0.2 nanoflowers which narrow the bandgap and serve as electron trapping centers, thus effectively enhancing the generation and separation rates of electron-hole pairs. As a result, the sunlight-irradiated BiOCl0.8Br0.2 film demonstrates outstanding photocatalytic performance in water purification such as degrading Rhodamine B (RhB) dye under visible light irradiation with 2-fold higher than its pristine state.
RESUMO
Curcumin-Fe(III) complex was prepared from Fe(NO3)3 · 9H2O precursor and curcumin by refluxing a slightly basic methanolic solution of their mixture with the objective of investigating its cytotoxicity. The enol form of curcumin ligand was established by FTIR, UV/Vis, (1)H NMR, and (13)C NMR spectroscopy. The as-prepared product was characterized by elemental analysis, FTIR, UV, and Mössbauer spectroscopic techniques. An octahedral high-spin Fe(III) complex was obtained, δ , 0.37 mms(-1); Q.S., 0.79 mms(-1); no magnetic relaxation was observed at liquid N2 temperature, neither reduction of Fe(III). The tested cytotoxicity of the as-prepared complex on four cancer cell lines indicated inhibition of the curcumin activity upon complexing with iron.