Influence of disinfection of caries effected dentin with different concentration of silver diamine fluoride, curcumin and Er, Cr:YSGG on adhesive bond strength to resin composite.

AIM: The aim of the study was to determine the effect of various disinfectants (CP, MB, 3.8 % SDF, 38 % SDF and ECL) on caries affected dentine (CAD) and its bond strength to composite restoration MATERIAL AND METHODS: Fifty carious mandibular teeth were collected based on the criteria of ICDAS (International Caries Detection and Assessment system). Specimens up to cement enamel junction were fixed in poly vinyl pipes. All caries molars were grinded using silicon grinding carbon disk and randomly assigned into five groups based on disinfecting regimes (n = 10). Group 1, Caries affected dentin (CAD) treated with MBP [100 mg/L]; Group 2, CAD treated with Curcumin photosensitizer (CP) [500 mg/L]; Group 3, CAD treated with 3.8 % SDF Group 4, CAD treated with 38 % SDF and group 5 sterile with Er,Cr:YSGG (ECL).Self-etch adhesive bond was smeared over the surface of all specimens followed by application of composite incrementally and light cured. Samples were debonded in a universal testing machine and shear bond strength (SBS) was noted in MegaPascal (MPa). The debonded surfaces were evaluated under stereomicroscope to determine the failure mode. For inter group comparison analysis of variance (ANOVA). Tukey HSD was applied for multiple group comparison. The significance level was kept at p < 0.05 RESULTS: The maximum bond strength was observed in group 2 CAD disinfected with CP (17.57 ± 0.85 MPa). Whereas, minimum bond strength values were presented by group 3 CAD disinfected with 38 % SDF (11.14 ± 0.29 MPa). CAD treated with MBP (14.21 ± 0.22 MPa) was comparable to group 5 (p > 0.05). Similarly, group 2 was found to be comparable to group 4 CAD disinfected with 3.8 % SDF (16.22±0.53 MPa) (p > 0.05). CONCLUSION: 3.8 % SDF and PDT with CP have shown potential to be adopted for dentin disinfection treatment without adversely affecting bond strength of CAD to composite resin.

Antimicrobial efficacy of silver diamine fluoride in comparison to photodynamic therapy and chlorhexidine on canal disinfection and bond strength to radicular dentin.

AIM: To assess the antimicrobial efficacy of Silver diamine fluoride (SDF), Sodium hypochlorite (NaOCl), Chlorhexidine (CHX) and Photodynamic therapy (PDT) in radicular dentin and subsequent bond strength of Fiber reinforced composite post (FRCP) to radicular dentin. MATERIAL AND METHODS: Forty extracted premolars were disinfected and decoronated up-to cement-o-enamel junction (CEJ). Canals were instrumented using crown-down technique, dried and filled with gutta percha. Post space was prepared with the help of peso reamers and inoculated with E. faecalis. Samples were randomly allocated into four groups based on chemical irrigation (n = 10). Group 1, canal disinfected with (PDT, MB), group 2 (5.25 % NaOCl +17 % EDTA), group 3 (3.8 % SDF) and group 4 (CHX). Specimens were tested with confocal laser scanning microscopy analysis (CLSM) to confirm the presence of E. faecalis. Fibre post were luted in root canal and sectioned at three levels (apical, middle and coronal). Push-out test was performed and failure analysis of debonded surfaces was evaluated using stereomicroscope. Live and dead cells after exposure were calculated in percentage. One-way analysis of variance (ANOVA) assessed the means and standard deviations of extrusion bond strength (EBS). Tukey multiple comparison tests was used to compare means of bond strength (p = 0.05). RESULTS: The maximum antimicrobial efficacy against E. faecalis was observed in group 2 which included canal disinfected with 5.25 % NaOCl and 17 % EDTA (64.41 ±â€¯1.22). Similarly, CHX showed lowest effectiveness as canal irrigant against E.faecalis (58.29 ±â€¯2.41). Intragroup comparison revealed highest bond strength for group 2 at all three level. Similarly, the lowest EBS was found in CHX group. Inter-group comparison confirmed comparable EBS at all root levels (apical, middle and coronal) for group 2 and group 3 (p > 0.05). CONCLUSION: Radicular dentin treated with 5.25 % NaOCl and 17 % EDTA displayed highest antimicrobial and bond strength scores. SDF and PDT can potentially be used in canal irrigation.