Synthesis, Fabrication, and Characterization of Functionalized Polydiacetylene Containing Cellulose Nanofibrous Composites for Colorimetric Sensing of Organophosphate Compounds.

Organophosphate (OP) compounds, a family of highly hazardous chemical compounds included in nerve agents and pesticides, have been linked to more than 250,000 annual deaths connected to various chronic diseases. However, a solid-state sensing system that is able to be integrated into a clothing system is rare in the literature. This study aims to develop a nanofiber-based solid-state polymeric material as a soft sensor to detect OP compounds present in the environment. Esters of polydiacetylene were synthesized and incorporated into a cellulose acetate nanocomposite fibrous assembly developed with an electrospinning technique, which was then hydrolyzed to generate more hydroxyl groups for OP binding. Scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), Instron® tensile tester, contact angle analyzer, and UV-Vis spectroscopy were employed for characterizations. Upon hydrolysis, polydiacetylene esters in the cellulosic fiber matrix were found unaffected by hydrolysis treatment, which made the composites suitable for OP sensing. Furthermore, the nanofibrous (NF) composites exhibited tensile properties suitable to be used as a textile material. Finally, the NF composites exhibited colorimetric sensing of OP, which is visible to the naked eye. This research is a landmark study toward the development of OP sensing in a protective clothing system.

Tunable Wettability of Biodegradable Multilayer Sandwich-Structured Electrospun Nanofibrous Membranes.

This research aims to develop multilayer sandwich-structured electrospun nanofiber (ENF) membranes using biodegradable polymers. Hydrophilic regenerated cellulose (RC) and hydrophobic poly (lactic acid) (PLA)-based novel multilayer sandwich-structures were created by electrospinning on various copper collectors, including copper foil and 30-mesh copper gauzes, to modify the surface roughness for tunable wettability. Different collectors yielded various sizes and morphologies of the fabricated ENFs with different levels of surface roughness. Bead-free thicker fibers were collected on foil collectors. The surface roughness of the fine fibers collected on mesh collectors contributed to an increase in hydrophobicity. An RC-based triple-layered structure showed a contact angle of 48.2°, which is comparable to the contact angle of the single-layer cellulosic fabrics (47.0°). The polar shift of RC membranes on the wetting envelope is indicative of the possibility of tuning the wetting behavior by creating multilayer structures. Wettability can be tuned by creating multilayer sandwich structures consisting of RC and PLA. This study provides an important insight into the manipulation of the wetting behavior of polymeric ENFs in multilayer structures for applications including chemical protective clothing.

Polydiacetylene Nanofiber Composites as a Colorimetric Sensor Responding To Escherichia coli and pH.

Polydiacetylenes (PDAs) are conjugative polymers that demonstrate color changes as a response to an external stimulus. In this study, 10,12-pentacosadiynoic acid (PCDA) was mixed with a supporting polymer including poly(ethylene oxide) (PEO) and polyurethane (PU), and the mixture solution was electrospun to construct fiber composites. The electrospun fibers were then photopolymerized using UV irradiation to produce PEO-PDA and PU-PDA nanofiber mats with a fiber diameter ranging from 130 nm to 2.5 µm. The morphologies of both PEO-PDA and PU-PDA nanofibers were dependent on electrospinning parameters such as the ratio of PCDA to PEO or PCDA to PU and the total polymer concentrations. Scanning electron microscopy images showed beaded fibers of PEO-PDA and PU-PDA at 2 and 18 w/v % concentrations, respectively. Smooth fibers were found when the solvent concentration was increased to 3.75 w/v % in PEO-PDA and 25 w/v % in PU-PDA fibers. Both PEO-PDA and PU-PDA nanofiber composites demonstrated excellent colorimetric responses to the presence of Escherichia coli ATCC25922 bacterial cells and the changes in pH as external stimuli. The nanofibers underwent a rapid colorimetric response when exposed directly to E. coli ATCC25922 grown on Luria-Bertani agar. The comparison between the PEO-PDA and PU-PDA suggested that the combination of PEO and PDA is favorable because it provides a sensitive response to the presence of E. coli. The results were compared with samples of a PDA polymer in the absence of a matrix polymer. The colorimetric response was similar when the PDA polymer and the PDA nanofiber composites were exposed to pH changes, and the color change was found to occur at pH 10 and enhanced at pH 11-13. The PDA-containing nanofiber composites showed stronger colorimetric responses than those of the PDA polymer only, suggesting their potential as biosensors and chemosensors.

Study of Polydiacetylene-Poly (Ethylene Oxide) Electrospun Fibers Used as Biosensors.

Polydiacetylene (PDA) is an attractive conjugated material for use in biosensors due to its unique characteristic of undergoing a blue-to-red color change in response to external stimuli. 10,12-Pentacosadiynoic acid (PCDA) and poly (ethylene oxide) (PEO) were used in this study to develop fiber composites via an electrospinning method at various mass ratios of PEO to PCDA, solution concentrations, and injection speeds. The PEO-PDA fibers in blue phase were obtained via photo-polymerization upon UV-light irritation. High mass ratios of PEO to PCDA, low polymer concentrations of spinning solution, and low injection speeds promoted fine fibers with small diameters and smooth surfaces. The colorimetric transition of the fibers was investigated when the fibers were heated at temperatures ranging from 25 °C to 120 °C. A color switch from blue to red in the fibers was observed when the fibers were heated at temperatures greater than 60 °C. The color transition was more sensitive in the fibers made with a low mass ratio of PEO to PCDA due to high fraction of PDA in the fibers. The large diameter fibers also promoted the color switch due to high reflectance area in the fibers. All of the fibers were analyzed using Fourier transform infrared spectroscopy (FT-IR) and differential scanning calorimetry (DSC) and compared before and after the color change occurred. The colorimetric transitional mechanism is proposed to occur due to conformational changes in the PDA macromolecules.