Development and Assessment of Bioactive Coatings for the Prevention of Recurrent Caries Around Resin Composite Restorations.

OBJECTIVE: To develop hydrophilic resin-based surface coatings containing bioactive agents (proanthocyanidins from Vitis vinifera and calcium silicate) and assess their protective role at the dentin and enamel margins of cervical restorations against demineralization under simulated conditions of high and low caries activity. METHODS: Suboptimal resin composite restorations were placed on cervical cavity preparations on buccal and lingual surfaces of thirty-two molars after a contamination protocol. Groups were divided according to the resin-based coatings (n=8): resin without bioactive (C), resin containing 2% enriched Vitis Vinifera (VVE), and resin coat containing 10% calcium silicate (CaSi). The control group did not receive a resin (NC). To simulate a hydrolyticenzymatic degradation, specimens were subjected to 2-month storage followed by incubation in esterase at 37°C for 8 days. Afterwards, recurrent caries was induced using a pH-proteolytic model on half of the specimens to simulate high caries activity, and the other half remained in simulated body fluid (SBF). Measurements of cross-section microhardness (KHN) and infiltration with rhodamine-B assessed the micropermeability (MP), the extent of demineralization (ED), and the demineralization area (DA). Data were analyzed using analysis of variance (ANOVA) and post-hoc tests (α=0.05). RESULTS: VVE and CaSi presented higher cross-sectional KHN values for enamel and dentin (p<0.001). The bioactive coatings resulted in lower MP, ED, and DA compared to NC (p<0.005) in enamel and dentin. CaSi coating preserved the enamel from demineralization (p=0.160). CONCLUSION: The application of bioactive coatings represents a potential strategy to protect the enamel-dentin margins of resin restorations.

Bioactive Materials Subjected to Erosion/Abrasion and Their Influence on Dental Tissues.

OBJECTIVE: The objective of this study was to evaluate the effect of erosion or erosion-abrasion on bioactive materials and adjacent enamel/dentin areas. METHODS AND MATERIALS: Enamel and dentin blocks (4×4×2 mm) were embedded side by side in acrylic resin, and a standardized cavity (1.2×4×1.5 mm) was prepared between them. Preparations were restored with the following materials: composite resin (Filtek Z350, control); experimental composite containing di-calcium phosphate dihydrate particles (DCPD); Giomer (Beautifil II), high viscosity glass ionomer cement (GIC, Fuji IX); and a resin-modified GIC (Fuji II LC). The specimens were submitted to two cycling models (n=10): erosion or erosion-abrasion. The challenges consisted of five-minute immersion in 0.3% citric acid solution, followed by 60-minute exposure to artificial saliva. Toothbrushing was carried out twice daily, 30 minutes after the first and last exposures to acid. Dental and material surface loss (SL, in µm) were determined by optical profilometry. Data were analyzed with Kruskal-Wallis and Dunn tests (α=0.05). RESULTS: Under erosion, for enamel, only the GIC groups presented lower SL values than Z350 (p<0.001 for Fuji IX and p=0.018 for Fuji II LC). For dentin, none of the materials showed significantly lower SL values than Z350 (p>0.05). For material, the GICs had significantly higher SL values than those of Z350 (p<0.001 for Fuji IX and p=0.002 for Fuji II LC). Under erosion-abrasion, the enamel SL value was significantly lower around Fuji II LC compared with the other materials (p<0.05). No significant differences were observed among groups for dentin SL (p=0.063). The GICs and Giomer showed higher SL values than Z350 (p<0.001 for the GICs and p=0.041 for Giomer). CONCLUSION: Both GIC-based materials were susceptible to erosive wear; however, they promoted the lowest erosive loss of adjacent enamel. Against erosion-abrasion, only Fuji II LC was able to reduce enamel loss. For dentin, none of the materials exhibited a significant protective effect.

Dimeric Proanthocyanidins on the Stability of Dentin and Adhesive Biointerfaces.

A dentin biomodification strategy with selective proanthocyanidin (PAC)-enriched extracts reinforces dentin and dentin-resin interfaces. Enrichment of the extracts according to the degree of polymerization allows exploration of bioactive principles of PACs and structure-activity relationships. This study investigated the sustained dentin matrix biomodification and dentin-resin bioadhesion of 2 fractions consisting exclusively of B-type PAC dimers with or without a single galloyl motif (specifically, DIMERG and DIMERNG) and their precursor material, enriched grape seed extract (e-GSE; Vitis vinifera). The biomodification potential was determined by long-term evaluation of the apparent modulus of elasticity and collagen solubility (hydroxyproline release). Chemical characterization of the dentin matrix was performed by attenuated total reflectance-Fourier-transform infrared spectroscopy. The bioadhesive properties were assessed by a microtensile bond strength test at different time points, and macro-hybrid layers were produced to verify the degree of conversion of the adhesive resin. Fractions consisting of DIMERG, DIMERNG, and their precursor, e-GSE, increased the modulus of elasticity at all time points and reduced collagen degradation. Specimens treated with DIMERNG remained stable throughout 12 mo of storage, whereas a significant drop in the modulus of elasticity was observed for the DIMERG and e-GSE groups at 6 mo. The fractions and precursor did not affect the degree of resin conversion at the hybrid layer. Changes in infrared resonances corresponding to collagen cross-links in the dentin matrix occurred for all treatments. Higher bond strength was observed for dentin treated with e-GSE as compared with DIMERG and DIMERNG; all biointerfaces remained stable after 12 mo. Nongalloylated PACs mediate stable dentin biomodification, which includes protective activity against collagen degradation and reinforcement of the anchoring dentin matrix. Collectively, PACs with a higher degree of oligomerization offer a robust bioadhesion between the hydrophilic dentin matrix and the hydrophobic adhesive.

Effect of Bioactive Composites on Microhardness of Enamel Exposed to Carious Challenge.

This study verified if experimental composites containing calcium phosphate nanoparticles exert a protective effect against enamel demineralization. Three experimental resin-based composites containing 60 vol% of fillers were manipulated. Filler phase was constituted by silanized barium glass and 0%, 10% or 20% (by volume) of dicalcium phosphate dihydrate (DPCD) nanoparticles functionalized with the monomer triethylene glycol dimethacrylate (TEGDMA). Cavities (10 x 2 x 2 mm) were prepared in bovine enamel and restored using one of the experimental materials (n=10). Specimens were exposed to pH cycling (demineralizing solution: pH 5.0/4h, remineralizing solution: pH 7.0/20h, 14 days). Enamel Knoop microhardness (100g/10s) was measured on the surface (SH) and after transversal sectioning up to 90 µm depth (cross-sectional microhardness, CSH). Microhardness values and the percent of microhardness loss were analyzed ANOVA/Tukey test and Student's paired t-test (alpha: 5%). The materials did not differ in respect to SH. Enamel adjacent to DCPD-containing composite restorations showed smaller reductions in CSH (-1.2% to -3.5%) than the enamel from control group (-12.5%), while CSH of enamel restored with resin-modified glass ionomer was similar to the other groups (-4.5%). DCPD-containing composites reduced enamel demineralization in comparison to a conventional composite.