Effects of Dentine Pretreatment Solutions Containing Flavonoids on the Resin Polymer-Dentine Interface Created Using a Modern Universal Adhesive.

The aim of the present study was to evaluate the influence of several experimental pretreatment crosslinker solutions on the resin polymer-dentine interface created using a representative universal adhesive system, by means of microtensile bond strength testing (µTBS), nanomechanical properties and ultramorphology confocal laser scanning microscopy (CLSM). Five experimental solutions containing different flavonoids were applied as dentine pretreatment after acid etching. A control pretreatment group containing no flavonoid was also employed. A representative modern universal adhesive was then applied, followed by a 3 mm thick composite built up. Specimens were sectioned into sticks and submitted to a µTBS test or nanoindentation analysis along the interface (24 h or 25,000 thermocycles). The ultramorphology of the polymer-resin interface was also evaluated using CLSM. The results were analyzed using two-way ANOVA and Bonferroni's post hoc test (α = 0.05). All flavonoids improved short- and long-term µTBS values (p < 0.01), while only some specific such solutions improved the nanomechanical properties (p < 0.05) and preserved the structural morphology of the interface after aging. Pretreatment of acid-etched dentine using specific flavonoid-containing solutions may be a promising approach to improve both the nanomechanical properties and the durability of modern universal adhesive systems.

In vivo temperature rise and acute inflammatory response in anesthetized human pulp tissue of premolars having Class V preparations after exposure to Polywave® LED light curing units.

OBJECTIVE: To evaluate the influence of light emitted from two Polywave®, LED light-curing units (LCU) on in vivo pulp temperature (PT) rise and signs of acute inflammatory response in pulps of human premolar having deep Class V preparations. METHODS: Sixty intact, first premolars from 15 volunteers requiring extraction received infiltrative anesthesia. A sterile thermocouple probe was inserted within the pulp tissue through a minute occlusal pulp exposure in only 45 teeth (n = 9) to continuously monitor PT (°C). A deep buccal Class V preparation was created, and the surface was exposed to light from a commercial Polywave LCU (Bluephase 20i (20i), Ivoclar Vivadent) or from an experimental LCU (Exp) using the exposure modes (EM): 1s/Exp and 2s/Exp, 10s/20i, 20s/20i, and 60s/20i. Peak PT and PT rise values above baseline (ΔT) data were evaluated using a one-way ANOVA followed by Tukey's post-hoc test (α = 5%). Teeth used for histological and immunohistochemical analyses (n = 3) were extracted approximately 2 h after exposure to the LCU. RESULTS: No significant difference in peak PT and ΔT values was noted between 2s/Exp and 20s/20i groups, which both exhibited higher values than 1s/Exp and 10s/20i groups (p < 0.001). Dilated and congested blood vessels were seen after exposure to 1s/Exp, 2s/Exp, or 60s/20i EMs. The expression of IL-1ß and TNF-α tended to be more intense when higher irradiance was delivered. SIGNIFICANCE: Although higher irradiance delivered over a short exposure caused lower PT rise than 5.5 °C, such EMs should be used with caution, as they have more potential to harm the pulp tissue.