Effects of Particle Size on the Dielectric, Mechanical, and Thermal Properties of Recycled Borosilicate Glass-Filled PTFE Microwave Substrates.

Low dielectric loss and low-cost recycled borosilicate (BRS) glass-reinforced polytetrafluoroethylene (PTFE) composites were fabricated for microwave substrate applications. The composites were prepared through a dry powder processing technique by dispersing different micron sizes (25 µm, 45 µm, 63 µm, 90 µm, and 106 µm) of the recycled BRS filler in the PTFE matrix. The effect of the filler sizes on the composites' thermal, mechanical, and dielectric properties was studied. The dielectric properties of the composites were characterised in the frequency range of 1-12 GHz using an open-ended coaxial probe (OCP) connected to a vector network analyser (VNA). XRD patterns confirmed the phase formation of PTFE and recycled BRS glass. The scanning electron microscope also showed good filler dispersion at larger filler particle sizes. In addition, the composites' coefficient of thermal expansion and tensile strength decreased from 12.93 MPa and 64.86 ppm/°C to 7.12 MPa and 55.77 ppm/°C when the filler size is reduced from 106 µm to 25 µm. However, moisture absorption and density of the composites increased from 0.01% and 2.17 g/cm3 to 0.04% and 2.21 g/cm3. The decrement in filler size from 106 µm to 25 µm also increased the mean dielectric constant and loss tangent of the composites from 2.07 and 0.0010 to 2.18 and 0.0011, respectively, while it reduced the mean signal transmission speed from 2.088 × 108 m/s to 2.031 × 108 m/s. The presented results showed that PTFE/recycled BRS composite exhibited comparable characteristics with commercial high-frequency laminates.

Effects of Recycled Fe2O3 Nanofiller on the Structural, Thermal, Mechanical, Dielectric, and Magnetic Properties of PTFE Matrix.

The purpose of this study was to improve the dielectric, magnetic, and thermal properties of polytetrafluoroethylene (PTFE) composites using recycled Fe2O3 (rFe2O3) nanofiller. Hematite (Fe2O3) was recycled from mill scale waste and the particle size was reduced to 11.3 nm after 6 h of high-energy ball milling. Different compositions (5-25 wt %) of rFe2O3 nanoparticles were incorporated as a filler in the PTFE matrix through a hydraulic pressing and sintering method in order to fabricate rFe2O3-PTFE nanocomposites. The microstructure properties of rFe2O3 nanoparticles and the nanocomposites were characterized through X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and high-resolution transmission electron microscopy (HRTEM). The thermal expansion coefficients (CTEs) of the PTFE matrix and nanocomposites were determined using a dilatometer apparatus. The complex permittivity and permeability were measured using rectangular waveguide connected to vector network analyzer (VNA) in the frequency range 8.2-12.4 GHz. The CTE of PTFE matrix decreased from 65.28×10-6/°C to 39.84×10-6/°C when the filler loading increased to 25 wt %. The real (ε') and imaginary (ε″) parts of permittivity increased with the rFe2O3 loading and reached maximum values of 3.1 and 0.23 at 8 GHz when the filler loading was increased from 5 to 25 wt %. A maximum complex permeability of 1.1-j0.07 was also achieved by 25 wt % nanocomposite at 10 GHz.