Effects of Graphene Oxide and Crumb Rubber on the Fresh Properties of Self-Compacting Engineered Cementitious Composite Using Response Surface Methodology.

Graphene oxide-modified rubberized engineered cementitious composite (GO-RECC) is attracting the attention of researchers because of the reported benefits of the GO and crumb rubber (CR) on the strength and deformation properties of the composite. While it is well established that GO negatively affects the workability of cementitious composites, its influence on the attainment of the desired self-compacting (SC) properties of ECC has not yet been thoroughly investigated, especially when combined with crumb rubber (CR). In addition, to simplify the number of trial mixes involved in designing SC-GO-RECC, there is a need to develop and optimize the process using Design of Experiment (DOE) methods. Hence, this research aims to investigate and model using response surface methodology (RSM), the combined effects of the GO and CR on the SC properties of ECC through the determination of T500, slump flow, V-funnel, and L-box ratio of the SC-GORECC as the responses, following the European Federation of National Associations Representing for Concrete (EFNARC) 2005 specifications. The input factors considered were the GO by wt.% of cement (0.02, 0.04, 0.06, and 0.08) and CR as a replacement of fine aggregate by volume (5, 10, and 15%). The results showed that increasing the percentages of GO and CR affected the fresh properties of the SC-GORECC adversely. However, all mixes have T500 of 2.4 to 5.2 s, slump flow of 645 to 800 mm, V-funnel time of 7.1 to 12.3 s, and L-box ratio (H2/H1) of 0.8 to 0.98, which are all within acceptable limits specified by EFNARC 2005. The developed response prediction models were well fitted with R2 values ranging from 91 to 99%. Through the optimization process, optimal values of GO and CR were found to be 0.067% and 6.8%, respectively, at a desirability value of 1.0.

Experimental study on fresh, mechanical properties and embodied carbon of concrete blended with sugarcane bagasse ash, metakaolin, and millet husk ash as ternary cementitious material.

In recent years, the research direction is shifted toward introducing new supplementary cementitious materials (SCM) in lieu of in place of Portland cement (PC) in concrete as its production emits a lot of toxic gases in the atmosphere which causes environmental pollution and greenhouse gases. SCM such as sugarcane bagasse ash (SCBA), metakaolin (MK), and millet husk ash (MHA) are available in abundant quantities and considered as waste products. The primary aim of this experimental study is to investigate the effect of SCBA, MK, and MHA on the fresh and mechanical properties of concrete mixed which contributes to sustainable development. A total of 228 concrete specimens were prepared with targeted strength of 25MPa at 0.52 water-cement ratio and cured at 28 days. It is found that the compressive strength and split tensile strength were enhanced by 17% and 14.28%, respectively, at SCBA4MK4MHA4 (88% PC, 4% SCBA, 4% MK, and 4% MHA) as ternary cementitious material (TCM) in concrete after 28 days. Moreover, the permeability and density of concrete are found to be reduced when SCBA, MK, and MHA are used separately and combined as TCM increases in concrete at 28 days, respectively. The results showed that the workability of the fresh concrete was decreased with the increase of the percentage of SCBA, MK, and MHA separately and together as TCM in concrete.