Selective capture of glycoproteins using lectin-modified nanoporous gold monolith.

The surface of nanoporous gold (np-Au) monoliths was modified via a flow method with the lectin Concanavalin A (Con A) to develop a substrate for separation and extraction of glycoproteins. Self-assembled monolayers (SAMs) of α-lipoic acid (LA) on the np-Au monoliths were prepared followed by activation of the terminal carboxyl groups to create amine reactive esters that were utilized in the immobilization of Con A. Thermogravimetric analysis (TGA) was used to determine the surface coverages of LA and Con A on np-Au monoliths which were found to be 1.31×10(18) and 1.85×10(15)moleculesm(-2), respectively. An in situ solution depletion method was developed that enabled surface coverage characterization without damaging the substrate and suggesting the possibility of regeneration. Using this method, the surface coverages of LA and Con A were found to be 0.989×10(18) and 1.32×10(15)moleculesm(-2), respectively. The selectivity of the Con A-modified np-Au monolith for the high mannose-containing glycoprotein ovalbumin (OVA) versus negative control non-glycosylated bovine serum albumin (BSA) was demonstrated by the difference in the ratio of the captured molecules to the immobilized Con A molecules, with OVA:Con A=2.3 and BSA:Con A=0.33. Extraction of OVA from a 1:3 mole ratio mixture with BSA was demonstrated by the greater amount of depletion of OVA concentration during the circulation with the developed substrate. A significant amount of captured OVA was eluted using α-methyl mannopyranoside as a competitive ligand. This work is motivated by the need to develop new materials for chromatographic separation and extraction substrates for use in preparative and analytical procedures in glycomics.

Electrochemical annealing of nanoporous gold by application of cyclic potential sweeps.

An electrochemical method for annealing the pore sizes of nanoporous gold (NPG) is reported. The pore sizes of NPG can be increased by electrochemical cycling with the upper potential limit being just at the onset of gold oxide formation. This study has been performed in electrolyte solutions including potassium chloride, sodium nitrate and sodium perchlorate. Scanning electron microscopy images have been used for ligament and pore size analysis. We examine the modifications of NPG due to annealing using electrochemical impedance spectroscopy, and cyclic voltammetry and offer a comparison of the surface coverage using the gold oxide stripping method as well as the method in which electrochemically accessible surface area is determined by using a diffusing redox probe. The effect of additives adsorbed on the NPG surface when subjected to annealing in different electrolytes as well as the subsequent structural changes in NPG are also reported. The effect of the annealing process on the application of NPG as a substrate for glucose electro-oxidation is briefly examined.

Lectin-carbohydrate interactions on nanoporous gold monoliths.

Monoliths of nanoporous gold (np-Au) were modified with self-assembled monolayers of octadecanethiol (C18-SH), 8-mercaptooctyl α-D-mannopyranoside (αMan-C8-SH), and 8-mercapto-3,6-dioxaoctanol (HO-PEG2-SH), and the loading was assessed using thermogravimetric analysis (TGA). Modification with mixed SAMs containing αMan-C8-SH (at a 0.20 mole fraction in the SAM forming solution) with either octanethiol or HO-PEG2-SH was also investigated. The np-Au monoliths modified with αMan-C8-SH bind the lectin Concanavalin A (Con A), and the additional mass due to bound protein was assessed using TGA analysis. A comparison of TGA traces measured before and after exposure of HO-PEG2-SH modified np-Au to Con A showed that the non-specific binding of Con A was minimal. In contrast, np-Au modified with octanethiol showed a significant mass loss due to non-specifically adsorbed Con A. A significant mass loss was also attributed to binding of Con A to bare np-Au monoliths. TGA revealed a mass loss due to the binding of Con A to np-Au monoliths modified with pure αMan-C8-SH. The use of mass losses determined by TGA to compare the binding of Con A to np-Au monoliths modified by mixed SAMs of αMan-C8-SH and either octanethiol or HO-PEG2-SH revealed that binding to mixed SAM modified surfaces is specific for the mixed SAMs with HO-PEG2-SH but shows a significant contribution from non-specific adsorption for the mixed SAMs with octanethiol. Minimal adsorption of immunoglobulin G (IgG) and peanut agglutinin (PNA) towards the mannoside modified np-Au monoliths was demonstrated. A greater mass loss was found for Con A bound onto the monolith than for either IgG or PNA, signifying that the mannose presenting SAMs in np-Au retain selectivity for Con A. TGA data also provide evidence that Con A bound to the αMan-C8-SH modified np-Au can be eluted by flowing a solution of methyl α-D-mannopyranoside through the structure. The presence of Con A proteins on the modified np-Au surface was also confirmed using atomic force microscopy (AFM). The results highlight the potential for application of carbohydrate modified np-Au monoliths to glycoscience and glycotechnology and demonstrate that they can be used for capture and release of carbohydrate binding proteins in significant quantities.