RESUMO
The objective of the study is to assess the precision of digital impressions in removable partial dentures through an in vitro study on the degree of abutment adaptation. A Kennedy Class III model with a prosthetic space between elements 43 and 47, featuring niches in the mesio-occlusal and cingulum regions, respectively. Conventional impressions were performed in subgroups CONC and CONM, while digital scanning was conducted in subgroups DIGC and DIGM. Simplified cobalt-chromium alloy frameworks were manufactured using the lost-wax technique on plaster and resin models. The degree of adaptation of the structures was evaluated by impressing the niches with condensation silicone, qualitatively assessing perforations, and quantitatively measuring the mold thickness under a stereomicroscope after cross-sectioning. Regular adaptation was more prevalent among the experimental groups. CONC showed a higher mean degree of abutment adaptation, while CONM had a lower mean. The study factors, impression technique, and type of abutment seat, were not statistically significant, with no interaction among the variables. Occlusal and cingulum abutment measurement points, in both impression techniques, showed no statistically significant difference. Digital scanning yielded better results in terms of abutment adaptation, with smaller average gaps between the abutment seat and the metal structure, making it clinically acceptable. The type of abutment seat and the impression technique did not have a statistically significant impact on abutment adaptation. The impression technique does not represent a factor influencing the adaptation of occlusal and cingulum abutments at different measurement points. (AU)
O Objetivo do estudo é valiar precisão da impressão digital em próteses parciais removíveis, por meio de um estudo in vitro sobre o grau de adaptação dos apoios. Um modelo Classe III de Kennedy com espaço protético entre o elemento 43 e 47, nichos na região mésio-oclusal e na do cíngulo. Foram realizadas impressões convencionais nos subgrupos CONC e CONM, e digitalização nos subgrupos DIGC e DIGM, onde estruturas simplificadas de liga de Co-Cr foram fabricadas usando a técnica de fundição perdida nos modelos de gesso e resina. O grau de adaptação das estruturas foi avaliado pela impressão dos nichos com silicone de condensação, qualitativamente as perfurações e quantitativamente a espessura do molde em um estereomicroscópio após seção transversal. A adaptação regular foi mais prevalente entre os grupos experimentais. CONC maior média do grau de adaptação do apoio, enquanto CONM menor média. Os fatores do estudo, técnica de impressão e tipo de assento de apoio, não foram estatisticamente significativos, sem interação entre as variáveis. Pontos de medição de apoio oclusal e de cíngulo, em ambas as técnicas de impressão, sem diferença estatisticamente significativa. A digitalização mostrou melhores resultados em relação ao grau de adaptação dos apoios, com menores lacunas médias entre o assento de apoio e a estrutura metálica, sendo clinicamente aceitável. O tipo de assento de apoio e a técnica de impressão não interferem estatisticamente na adaptação dos apoios. A técnica de impressão não representa um fator que influencie a adaptação de apoios oclusais e de cíngulo em diferentes pontos de medição. (AU)
RESUMO
ABSTRACT The use of removable partial dentures is considered a common and inexpensive treatment option to rehabilitate edentulous areas. The aim of this study was to evaluate the effect of different materials for provisional removable partial dentures, an in vitro study on surface roughness and fracture resistance. Thermopolymerizable acrylic resin and thermoplastic resin specimens with dimensions of 10 x 10 x 2 mm (blocks) (n=10) and with dimensions of 65 x 20 x 3 mm (bars) (n=10 were analyzed for their surface roughness (Ra) and three-point flexural strength test. All specimens were subjected to oven aging for 60 days at 37°C±0.5°C in distilled water. The statistical analysis was performed with a significance level of 5%, and the surface roughness data were submitted to the Two-way Anova statistical test (P < 0.05) and the mechanical strength data were subjected to One-way Anova statistical test (P < 0.05). For roughness, the factor resin type (P = 0.000) and the factor aging (P = 0.000) were statically significant, as well as showing interaction (P = 0.228). The Thermopolymerizable acrylic resin had the lowest mean roughness values compared to the thermoplastic resin and showed no statistical difference after aging. The same scenario was repeated for flexural strength values; Thermopolymerizable acrylic resin was statistically superior to thermoplastic resin (P = 0.000). Thermopolymerized acrylic resin showed lower surface roughness values and higher flexural strength values compared to thermoplastic resin.
RESUMO O uso de próteses parciais removíveis é considerado uma opção de tratamento comum e de baixo custo para reabilitar áreas edêntulas. O objetivo deste estudo foi avaliar o efeito de diferentes materiais para próteses parciais removíveis provisórias, um estudo in vitro sobre rugosidade superficial e resistência à fratura. Espécimes de resina acrílica termopolimerizável e de resina termoplástica com dimensões de 10 x 10 x 2 mm (blocos) (n = 10) e de 65 x 20 x 3 mm (barras) (n = 10) foram analisados em rugosidade superficial média (Ra) e teste de resistência à flexão de três pontos. Todos os espécimes foram submetidos ao envelhecimento em estufa por 60 dias a 37 ° C ± 0,5 ° C em água destilada. A análise estatística se deu com nível de significância de 5%, e os dados de rugosidade superficial foram submetidos ao teste estatístico Anova dois fatores (P <0,05) e os dados de resistência mecânica foram submetidos ao teste estatístico Anova um fator (P <0,05). Para rugosidade, o fator tipo resina (P = 0,000) e o fator envelhecimento (P = 0,000) foram estatisticamente significantes, além de apresentar interação (P = 0,228). A resina acrílica termopolimerizável apresentou menores valores médios de rugosidade em relação à resina termoplástica e não apresentou diferença estatística após envelhecimento. O mesmo cenário foi repetido para valores de resistência à flexão; a resina acrílica termopolimerizável foi estatisticamente superior à resina termoplástica (P = 0,000). A resina acrílica termopolimerizada apresentou menores valores de rugosidade superficial e maiores valores de resistência à flexão em relação à resina termoplástica.