Effect of Different Wax Pattern Manufacturing Techniques on the Marginal Fit of Lithium Disilicate Crowns.

Purpose: The present study evaluated the marginal gap of lithium disilicate crowns fabricated through three different wax pattern techniques; Conventional, Milling and 3D-printing. Materials and Methods: Thirty stone models were replicated from a stainless-steel model representing a prepared tooth; ten were sent to make conventional wax patterns while the remaining were sent to a digital dental scanner. The computer aided design was completed and STL (Standard Tessellation Language) files were sent to either milling or 3D-printing machines. All wax patterns (n = 30) were pressed, and a stabilizing instrument was used to secure the crowns on the master model. The marginal gap was measured at 18 points for each crown using a digital microscope (µm) (n = 540) and compared using One-way ANOVA (p ≤ 0.05). Results: There was a significant difference in the marginal gap value between all three groups (p < 0.01) where the milled group showed the least mean gap (28.87 ± 30.18 µm), followed by 3D printed (47.85 ± 27.44 µm), while the highest mean marginal gap was found in the conventional group (63.49 ± 28.05 µm). Conclusion: Milled and 3D-printed wax patterns produced better fitting crowns compared to conventional techniques.

The effect of the digital manufacturing technique of cantilevered implant-supported frameworks on abutment screw preload.

PURPOSE: The purpose of this study was to investigate the misfit and screw preload at the implant abutment connection of implant supported fixed dental prosthesis with cantilever (ICFDP) manufactured using different digital manufacturing techniques and to compare the screw preload before and after cyclic loading. MATERIALS AND METHODS: Mandibular jaw model with four intra-foraminal implants was scanned using digital scanner. Stereolithography file was used to design a framework with nonengaging (NE) abutments and 10 mm cantilever distal to one terminal implant. Five frameworks were constructed using combined digital-conventional techniques (CAD-cast), and five frameworks were constructed using three-dimensional printing (3DP). Additional CAD-cast framework was constructed in a way that ensures passive fit (PF) to use as control. Scanning electron microscope (SEM) measured the implant abutment connection misfit. Sixty screws were used on the corresponding frameworks. Screws were torqued and pre-cyclic loading reverse torque value (RTV) was recorded. Frameworks were subjected to 200,000 loading cycles with a loading point 9 mm from the center of terminal implants adjacent to the cantilever and post-cyclic loading RTVs were recorded. RESULTS: Microscopic readings showed significant differences between frameworks. PF demonstrated the lowest measurements of 16.04 (2.6) µm while CAD-cast demonstrated the highest measurements of 29.2 (3.1) µm. In all groups, RTVs were significantly lower than the applied torque. Post-cyclic loading RTV was significantly lower than pre-cyclic loading RTV in PF and 3DP frameworks. Differences in RTVs between the three manufacturing techniques were insignificant. CONCLUSION: Although CAD-cast and three-dimensionally printed (3DP) both produce frameworks with clinically acceptable misfit, 3DP might not be the technique of choice for maintaining screw's preload stability under an aggressive loading situation.