Defects oriented hydrothermal synthesis of TiO2 and MnTiO2 nanoparticles as photocatalysts for wastewater treatment and antibacterial applications.

Pure and manganese-doped titanium dioxide nanoparticles (MnTiO2-NPs) were synthesized by the defect-oriented hydrothermal approach. The synthesized material was then characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Energy dispersive X-ray spectroscopy (EDX), and UV-visible spectroscopy (UV-Vis). The agar well diffusion method assessed the antibacterial efficiency of TiO2 and MnTiO2-NPs against E. coli and S. aureus. Zone of inhibition (ZOI) formed by pure TiO2 was observed as 12 mm and 11.5 mm against E. coli and S. aureus, while for MnTiO2-NPs it was observed as 19 mm (E. coli) and 21 mm (S. aureus). The concentration of synthesized nanoparticles (10 mg/ml, and 20 mg/ml) was used for antibacterial studies. The efficacy of the pure and MnTiO2-NPs as an active photocatalyst for the degradation of methylene blue (MB) dye was also assessed using a UV light. It was observed that the photodegradation efficiency of 1 g of MnTiO2-NPs was higher than the same amount of pure TiO2. The results suggest that the photocatalyst concentration directly impacts the photodegradation of MB dye. The pH value was found to influence the photodegradation of MB dye at higher pH values. Based on the obtained results, MnTiO2-NPs were observed as a promising agent for microbial resistance and water remediation.

Photocatalytic Synthesis of Coumarin Derivatives Using Visible-Light-Responsive Strawberry Dye-Sensitized Titanium Dioxide Nanoparticles.

This study presents a novel method for the photocatalytic synthesis of 4-aryl-6-(3-coumarinyl) pyrimidin-2 (1H)-ones (a coumarin derivative) using strawberry dye-sensitized TiO2 (SD-TiO2) under visible light. The synthesis of 4-aryl-6-(3-coumarinyl) pyrimidin-2 (1H)-ones was achieved through a three-component, one-pot condensation reaction involving 3-acetyl coumarin, aldehydes, and urea, utilizing SD-TiO2 as a reusable and innovative photocatalyst at room temperature. The resulting SD-TiO2 photocatalyst was thoroughly characterized using FT-IR, XPS, XRD, SEM, and BET. The efficacy of SD-TiO2 was evaluated by comparing it to pristine TiO2 in terms of photocatalytic activity, and the optimal conditions for the synthesis process were determined. Notably, the SD-TiO2 photocatalyst exhibited a maximum yield of the compound, reaching up to 96% in just 30 min with a catalyst concentration of 1 mg/mL. This yield surpasses traditional thermal procedures employing reflux conditions, where 1 mg/mL of SD-TiO2 is sufficient to complete the reaction. The resulting 4-aryl-6-(3-coumarinyl) pyrimidin-2 (1H)-ones were further characterized using 1H-NMR and 13C-NMR. Moreover, the stability of the SD-TiO2 photocatalyst was confirmed through recyclability experiments and spectroscopic characterization, demonstrating its practicality for up to three consecutive reaction cycles.

Scalable Synthesis of Oxygen Vacancy-Rich Unsupported Iron Oxide for Efficient Thermocatalytic Conversion of Methane to Hydrogen and Carbon Nanomaterials.

Thermocatalytic methane decomposition (TCMD) involving metal oxides is a more environmentally friendly and cost-effective strategy for scalable hydrogen fuel production compared to traditional methane steam reforming (MSR), as it requires less energy and produces fewer CO/CO2 emissions. However, the unsupported metal oxide catalysts (such as α-Fe2O3) that would be suited for this purpose exhibit poor performance in TCMD. To overcome this issue, a novel strategy was developed as a part of this work, whereby oxygen vacancies (OVs) were introduced into unsupported α-Fe2O3 nanoparticles (NPs). Systematic characterization of the obtained materials through analytical techniques demonstrated that mesoporous nanostructured unsupported α-Fe2O3 with abundant oxygen vacancies (OV-rich α-Fe2O3 NPs) could be obtained by direct thermal decomposition of ferric nitrate at different calcination temperatures (500, 700, 900, and 1100 °C) under ambient conditions. The thermocatalytic activity of the resulting OV-rich α-Fe2O3 NPs was assessed by evaluating the methane conversion, hydrogen formation rate, and amount of carbon deposited. The TCMD results revealed that 900 °C was the most optimal calcination temperature, as it led to the highest methane conversion (22.5%) and hydrogen formation rate (47.0 × 10-5 mol H2 g-1 min-1) after 480 min. This outstanding thermocatalytic performance of OV-rich α-Fe2O3 NPs is attributed to the presence of abundant OVs on their surfaces, thus providing effective active sites for methane decomposition. Moreover, the proposed strategy can be cost-effectively scaled up for industrial applications, whereby unsupported metal oxide NPs can be employed for energy-efficient thermocatalytic CH4 decomposition into hydrogen fuel and carbon nanomaterials.

Solar-Driven Thermocatalytic Synthesis of Octahydroquinazolinone Using Novel Polyvinylchloride (PVC)-Supported Aluminum Oxide (Al2O3) Catalysts.

The chemical industry is one of the main fossil fuel consumers, so its reliance on sustainable and renewable resources such as wind and solar energy should be increased to protect the environment. Accordingly, solar-driven thermocatalytic synthesis of octahydroquinazolinone using polyvinylchloride (PVC)-supported aluminum oxide (Al2O3) as a catalyst under natural sunlight is proposed in this work. The Al2O3/PVC catalysts were characterized by FT-IR, SEM, BET, XRD, and XPS techniques. The obtained results indicate that the yield and reaction time can be modified by adjusting the molar ratio of the catalyst. To investigate the stability of the catalyst, the spent catalyst was reused in several reactions. The results indicated that, when a 50% Al2O3 catalyst is employed in an absolute solar heat, it performs exceptionally well in terms of yield (98%) and reaction time (35 min). Furthermore, the reaction times and yield of octahydroquinazolinone derivatives with an aryl moiety were superior to those of heteroaryl. All the synthesized compounds were well characterized by FT-IR, 1H-NMR, and 13C-NMR. The current work introduces a new strategy to use solar heat for energy-efficient chemical reactions using a cost-effective, recyclable environmentally friendly PVC/Al2O3 catalyst that produces a high yield.

Classification, processing, and applications of bioink and 3D bioprinting: A detailed review.

With the advancement in 3D bioprinting technology, cell culture methods can design 3D environments which are both, complex and physiologically relevant. The main component in 3D bioprinting, bioink, can be split into various categories depending on the criterion of categorization. Although the choice of bioink and bioprinting process will vary greatly depending on the application, general features such as material properties, biological interaction, gelation, and viscosity are always important to consider. The foundation of 3D bioprinting is the exact layer-by-layer implantation of biological elements, biochemicals, and living cells with the spatial control of the implantation of functional elements onto the biofabricated 3D structure. Three basic strategies underlie the 3D bioprinting process: autonomous self-assembly, micro tissue building blocks, and biomimicry or biomimetics. Tissue engineering can benefit from 3D bioprinting in many ways, but there are still numerous obstacles to overcome before functional tissues can be produced and used in clinical settings. A better comprehension of the physiological characteristics of bioink materials and a higher level of ability to reproduce the intricate biologically mimicked and physiologically relevant 3D structures would be a significant improvement for 3D bioprinting to overcome the limitations.

Development of highly-reproducible hydrogel based bioink for regeneration of skin-tissues via 3-D bioprinting technology.

3-D Bioprinting is employed as a novel approach in biofabrication to promote skin regeneration following chronic-wounds and injury. A novel bioink composed of carbohydrazide crosslinked {polyethylene oxide-co- Chitosan-co- poly(methylmethacrylic-acid)} (PEO-CS-PMMA) laden with Nicotinamide and human dermal fibroblast was successfully synthesized via Free radical-copolymerization at 73 °C. The developed bioink was characterized in term of swelling, structural-confirmation by solid state 13C-Nuclear Magnetic Resonance (NMR), morphology, thermal, 3-D Bioprinting via extrusion, rheological and interaction with DNA respectively. The predominant rate of gelation was attributed to the electrostatic interactions between cationic CS and anionic PMMA pendant groups. The morphology of developed bioink presented a porous architecture satisfying the cell and growth-factor viability across the barrier. The thermal analysis revealed two-step degradation with 85 % weight loss in term of decomposition and molecular changes in the bioink moieties By applying low pressure in the range of 25-50 kPa, the optimum reproducibility and printability were determined at 37 °C in the viscosity range of 500-550 Pa. s. A higher survival rate of 92 % was observed for (PEO-CS-PMMA) in comparison to 67 % for pure chitosan built bioink. A binding constant of K ≈ 1.8 × 106 M-1 recognized a thermodynamically stable interaction of (PEO-CS-PMMA) with the Salmon-DNA. Further, the addition of PEO (5.0 %) was addressed with better self-healing and printability to produce skin-tissue constructs to replace the infected skin in human.

Enhanced Optical and Antibacterial Activity of Hydrothermally Synthesized Cobalt-Doped Zinc Oxide Cylindrical Microcrystals.

Cobalt (Co) doped zinc oxide (ZnO) microcrystals (MCs) are prepared by using the hydrothermal method from the precursor's mixture of zinc chloride (ZnCl2), cobalt-II chloride hexahydrate (CoCl2·6H2O), and potassium hydroxide (KOH). The smooth round cylindrical morphologies of the synthesized microcrystals of Co-doped ZnO show an increase in absorption with the cobalt doping. The antibacterial activity of the as-obtained Co-doped ZnO-MCs was tested against the bacterial strains of gram-negative (Escherichia coli, Klebsiella pneumonia) and gram-positive bacteria (Staphylococcus aureus, Streptococcus pyogenes) via the agar well diffusion method. The zones of inhibition (ZOI) for Co-doped ZnO-MCs against E. coli and K. pneumoniae were found to be 17 and 19 mm, and 15 and 16 mm against S. Aureus and S. pyogenes, respectively. The prepared Co-doped ZnO-MCs were thus established as a probable antibacterial agent against gram-negative bacterial strains.

Synergistic effects of Cu-doped ZnO nanoantibiotic against Gram-positive bacterial strains.

A viable hydrothermal technique has been explored for the synthesis of copper doped Zinc oxide nanoparticles (Cu-doped ZnO-NPs) based on the precursor's mixture of Copper-II chloride dihydrate (CuCl2.2H2O), Zinc chloride (ZnCl2), and potassium hydroxide (KOH). X-ray diffraction (XRD) reported the hexagonal wurtzite structure of the synthesized Cu-doped ZnO-NPs. The surface morphology is checked via field emission scanning electron microscopy (FE-SEM), whereas, the elemental compositions of the samples were confirmed by Raman, and X-ray photoelectron spectroscopy (XPS), respectively. The as-obtained ZnO-NPs and Cu-doped ZnO-NPs were then tested for their antibacterial activity against clinical isolates of Gram-positive (Staphylococcus aureus, Streptococcus pyogenes) and Gram-negative (Escherichia coli, Klebsiella pneumonia) bacteria via agar well diffusion method. The zone of inhibition (ZOI) for Cu-doped ZnO-NPs was found to be 24 and 19 mm against S. Aureus and S. pyogenes, and 18 and 11 mm against E. coli and K. pneumoniae, respectively. The synthesized Cu-doped ZnO-NPs can thus be found as a potential nano antibiotic against Gram-positive multi-drug resistant bacterial strains.

Structural, Optical and Antibacterial Efficacy of Pure and Zinc-Doped Copper Oxide against Pathogenic Bacteria.

Copper oxide and Zinc (Zn)-doped Copper oxide nanostructures (CuO-NSs) are successfully synthesized by using a hydrothermal technique. The as-obtained pure and Zn-doped CuO-NSs were tested to study the effect of doping in CuO on structural, optical, and antibacterial properties. The band gap of the nanostructures is calculated by using the Tauc plot. Our results have shown that the band gap of CuO reduces with the addition of Zinc. Optimization of processing conditions and concentration of precursors leads to the formation of pine needles and sea urchin-like nanostructures. The antibacterial properties of obtained Zn-doped CuO-NSs are observed against Gram-negative (Pseudomonas aeruginosa, Klebsiella pneumonia, Escherichia coli) and Gram-positive (Staphylococcus aureus) bacteria via the agar well diffusion method. Zn doped s are found to have more effective bacterial resistance than pure CuO. The improved antibacterial activity is attributed to the reactive oxygen species (ROS) generation.

Antimicrobial Activity of Synthesized 2-Methylthiobenzo[g][1,2,4]- triazolo[1,5-a]quinazoline Derivatives.

BACKGROUND: The present study was carried out to evaluate the antimicrobial activity of a synthesized 2-methylthio-benzo[g][1,2,4]triazolo[1,5- a]quinazoline series. The compounds (1-21) were tested against a variety of Gram-positive bacterial species including Bacillus subtilis (RCMB 01001 69-3), Enterococcus faecalis (RCMB 0100154-2), Staphylococcus aureus (RCMB 0100183-9), Staphylococcus epidermidis (RCMB 0100183-9) and Streptococcus pyogenes (RCMB 0100172-5). In addition, Gram-negative bacteria were also tested including Pseudomonas aeruginosa (RCMB 0100243-5), Escherichia coli (RCMB 010052-6), Proteus mirabilis (RCMB 01002 54-2), Klebsiella oxytoca (RCMB 01002 83-4) and Enterobacter cloacae (RCMB 01002 64-5). Furthermore, their activities were screened against ten types of fungi i.e. Aspergillus fumigatus (RCMB 02568), Syncephalastrum racemosum (RCMB 05922), Geotricum candidum (RCMB 05097), Candida albicans (RCMB 05036), Aspergillus niger (RCMB 02724), Cryptococcus neoformans (RCMB 05642), Candida tropicalis (RCMBA 05239), Penicillium expansum (RCMB 01924), Microsporum canis (RCMB 0834) and Trichophyton mentagrophytes (RCMB 0925). METHODS: Evaluation of antimicrobial activity was performed using agar well diffusion method in comparison with ampicillin and gentamycin as antibacterial reference drugs, and amphotericin B as antifungal reference drug. The minimum inhibitory concentration (MIC) was determined using the broth double dilution technique. RESULTS: The MIC values of the tested compounds were reported in .g/mL in which ampicillin, gentamicin and amphotericin B were used as standard reference drugs. The obtained results revealed that compounds 3, 4, 7, 8, 9, 10, 11, 14, 17, 18, 19, 20 and 21 showed significant antimicrobial activity against six bacterial and six fungal strains. CONCLUSION: The promising compounds could be employed as useful scaffolds for building of new derivatives with more potent antimicrobial effects.

Efficient hydrodeoxygenation of biomass-derived ketones over bifunctional Pt-polyoxometalate catalyst.

Acidic heteropoly salt Cs(2.5)H(0.5)PW(12)O(40) doped with Pt nanoparticles is a highly active and selective catalyst for one-step hydrogenation of methyl isobutyl and diisobutyl ketones to the corresponding alkanes in the gas phase at 100 °C with 97-99% yield via metal-acid bifunctional catalysis.