RESUMO
Structural optimizations of the piezoelectric layer in nanogenerators have been predicted to enhance the output performance in terms of the figure of merit. Here, we report the effect of dielectric constant on electrical outputs of piezoelectric nanogenerator using ZnO/PDMS composites with varied ZnO coverages. The dielectric constant of piezoelectric layers was adjusted from 3.37 to 6.75. The electrical output voltage of 9 mV was achieved in the nanogenerator containing the ZnO/PDMS composite with the dielectric constant of 3.46, which is an 11.3-fold enhancement compared to the value of the nanogenerator featuring the composite with high dielectric constants. Significantly, lowering the dielectric constant of the piezoelectric layer improves the electrical output performance of piezoelectric nanogenerators.
RESUMO
We prepared ZnO nanocomposites with WO3 or CuO nanostructures to improve the photocatalytic performance of ZnO nanostructures. Characterization of the nanocomposites using scanning electron microscopy, x-ray diffraction, UV-vis spectrometry and photoluminescence revealed the morphologies and wide light absorption range of the materials. The highest current densities of WO3/ZnO and CuO/ZnO nanocomposites were 1.28 mA cm-2 and 2.49 mA cm-2 at 1.23 V (versus a reversible hydrogen electrode) under AM 1.5 100 mW cm-2, which are ~1.2- and 3.5-fold greater than those of bare ZnO nanostructures, respectively. The easy fabrication process suggests that nanocomposites with narrow bandgap materials, such as WO3 and CuO, will improve the performance of electrochemical and optoelectrical devices such as dye-sensitized solar cells and biosensors.