RESUMO
Objective: To evaluate the clinical efficacy of novel titania-nanoparticle reinforced bonding agent on post-restorative sensitivity in patients. Methods: This triple-blinded, randomized clinical trial included participants (n = 60) having Class- I and II cavitations with a minimum cavity depth of 3mm at Department of Operative Dentistry & Endodontics, School of Dentistry, Shaheed Zulfiqar Ali Bhutto Medical University, Islamabad from January 5, 2023, to June 20, 2023. They were randomly assigned into two groups A and B (n = 30). After informed consent, restorative intervention was accomplished using an etch-and-rinse adhesive strategy. In Group-A, titania-nanoparticle-incorporated bonding agent was used for composite restoration, while in Group-B, bonding agent without nanoparticles was used. The primary outcome was assessed using Visual Analogue Scale mean score. Participants were instructed to rate their sensitivity status at follow-ups: 24 hours, one week, and one month. Mann-Whitney U test was employed to compare sensitivity between the two groups. Results: According to results of this trial, a significant difference was observed between two groups after 24 hours (p = 0.004) and one week (p = 0.002). However, no discernible difference was observed after one month (p = 0.643). Conclusion: Post-restorative sensitivity in patients with composite restorations was reduced using titania-reinforced bonding agents as compared to bonding agents without nanoparticles. This shows that inclusion of titania nanoparticles into adhesive dentistry could be beneficial in resolving post-restorative sensitivity occurring with composite restorations.