RESUMO
An active film composed of corn starch/κ-carrageenan and ethanolic grape seed extract (0, 1, 3, and 5 wt% of GSE on corn starch basis) were successfully prepared using the solvent casting technique. The effects of the different concentrations of ethanolic grape seed extract (GSE) on the physicochemical properties, antioxidant properties, and antibacterial properties of CS/κC films were analyzed. The results showed that the addition of GSE inhibited the recrystallization of starch in the composite film. The glass transition temperature of composite film is 121.65 °C. With the addition of GSE, the surface roughness of the composite film increased, and the cross-section displayed a stratification phenomenon. Meanwhile, when GSE was added to the composite film, the tensile strength of the composite film decreased (3.50 ± 0.27 MPa), the elongation at break increased (36.87 ± 2.08%), and the WVP increased (1.58 ± 0.03 g mm/m2·d· kPa). With the increase of the concentration of GSE in the composite film, the a* value and b* value of the composite film increase, the L* value decreases, and the opacity increases. The lipid oxidation test proved that the composite films containing 1% GSE has a significant inhibitory effect on the oxidation of lard (p < 0.05). The above results indicate that the GSE can be used as a food-grade packaging material and has a good application prospect in the food industry.
RESUMO
Using corn starch (CS) and κ-carrageenan(κC) as the raw material and active composite, respectively, films containing different concentrations of ethanol extract of onion skin were prepared. The effects of different concentrations of ethanol extract of onion skin (EEOS) on the physicochemical properties, as well as the antioxidant and antibacterial properties, of CS/κC films were also discussed. The addition of ethanol extract of onion skin inhibited the recrystallization of starch molecules in the composite films. It affected the microstructure of the composite films. The color of the composite films was deepened, the brightness was reduced, and the opacity was increased. Water vapor permeability increased, tensile strength decreased, and elongation at the break increased. The glass-transition temperature decreased. The clearance of DPPH radicals and ABTS cation radicals increased. Moreover, when the concentration of EEOS was 3%, the antioxidant effect of the films on oil was greatly improved and could effectively inhibit Staphylococcus aureus and Escherichia coli. The above results showed that adding ethanol extract of onion skin improved the physicochemical properties and biological activities of the CS/κC composite films, so CS/κC/EEOS composite films can be used as an active packaging material to extend food shelf-life. These results can provide a theoretical basis for the production and application of corn starch/κ-carrageenan/ethanol extract of onion skin composite films.