Synthesis of Tungsten Carbides in a Copper Matrix by Spark Plasma Sintering: Microstructure Formation Mechanisms and Properties of the Consolidated Materials.

In this study, the synthesis of tungsten carbides in a copper matrix by spark plasma sintering (SPS) is conducted and the microstructure formation mechanisms of the composite materials are investigated. The reaction mixtures were prepared by the high-energy mechanical milling (MM) of W, C and Cu powders. The influence of the MM time and SPS temperature on the tungsten carbide synthesis in an inert copper matrix was analyzed. It was demonstrated that the milling duration is a critical factor for creating the direct contacts between the W and C reactants and increasing the reactive transformation degree. A WC-W2C-Cu composite was fabricated from the W-C-3Cu powder mixture milled for 10 min and subjected to SPS at a temperature of 980 °C for 5 min. The formation of unconventional microstructures with Cu-rich regions is related to inter-particle melting during SPS. The WC-W2C-Cu composite showed a promising combination of mechanical and functional properties: a hardness of 300 HV, an electrical conductivity of 24% of the International Annealed Copper Standard, a residual porosity of less than 5%, a coefficient of friction in pair with a WC-6Co counterpart of 0.46, and a specific wear rate of the material of 0.52 × 10-5 mm3 N-1 m-1.

Crystallization of Ti33Cu67 metallic glass under high-current density electrical pulses.

We have studied the phase and structure evolution of the Ti33Cu67 amorphous alloy subjected to electrical pulses of high current density. By varying the pulse parameters, different stages of crystallization could be observed in the samples. Partial polymorphic nanocrystallization resulting in the formation of 5- to 8-nm crystallites of the TiCu2 intermetallic in the residual amorphous matrix occurred when the maximum current density reached 9.7·108 A m-2 and the pulse duration was 140 µs, though the calculated temperature increase due to Joule heating was not enough to reach the crystallization temperature of the alloy. Samples subjected to higher current densities and higher values of the evolved Joule heat per unit mass fully crystallized and contained the Ti2Cu3 and TiCu3 phases. A common feature of the crystallized ribbons was their non-uniform microstructure with regions that experienced local melting and rapid solidification.PACS: 81; 81.05.Bx; 81.05.Kf.