The effect of thermal cycling on the shear bond strength of porcelain/Ti-6Al-4V interfaces.

The aim of the study was to evaluate the effect of thermal cycling on the shear bond strength of the porcelain/Ti-6Al-4V interfaces prepared by two different processing routes and metallic surface conditions. Polished and SiO2 particle abraded Ti-6Al-4V alloy and Triceram bonder porcelain were used to produce the interfaces. Porcelain-to-metal specimens were processed by conventional furnace firing and hot pressing. Thermal cycling was performed in Fusayama's artificial saliva for 5000 cycles between 5 ± 1 and 60 ± 2°C. After thermal cycling, shear bond tests were carried out by using a custom-made stainless steel apparatus. The results were analyzed using t-Student test and non-parametric Kruskal-Wallis test (p<0.01). Most of the polished-fired specimens were fractured during thermal cycling; thus, it was not possible to obtain the shear bond strength results for this group. Sandblasted-fired, polished-hot pressed, and sandblasted-hot pressed specimens presented the shear bond strength values of 76.2 ± 15.9, 52.2 ± 23.6, and 59.9 ± 22.0 MPa, respectively. Statistical analysis indicated that thermal cycling affected the polished specimens processed by firing, whereas a significant difference was not observed on the other groups.

How do titanium and Ti6Al4V corrode in fluoridated medium as found in the oral cavity? An in vitro study.

The purpose of this work was to evaluate the corrosion of commercially pure (CP) titanium and Ti6Al4V in vitro at different F(-) concentrations regularly found in the oral cavity by using different electrochemical tests and surface analysis techniques. electrochemical impedance spectroscopy (EIS), open circuit potential (OCP) and potentiodynamic polarization tests were associated to advanced characterization techniques such as SEM, EDS, AFM, ICP-MS and XPS. OCP tests revealed a higher reactivity of both CP titanium and Ti6Al4V at 12,300 ppm F(-) concentration than that recorded at 227 ppm F(-). Also, a significant decrease of the corrosion resistance of both materials was noticed by EIS in fluoride solutions. Material loss caused by corrosion was noticed on titanium surfaces by SEM and AFM in the presence of high F(-) concentration. CP titanium degraded by pitting corrosion while Ti6Al4V suffered from general corrosion showing micro-cracks on surface. Furthermore, a high release of metallic ions from the test samples after immersion at high F(-) concentrations was detected by ICP-MS, that can be potentially toxic to oral tissues.

Mechanical and chemical analyses across dental porcelain fused to CP titanium or Ti6Al4V.

The aim of this study was to evaluate the evolution of mechanical properties and chemical variation across veneering dental porcelain fused to different titanium-based substrates. Test samples were synthesized by fusing dental feldspar-based porcelain onto commercially pure titanium grade II or Ti6Al4V alloy. Samples were cross-sectioned at angles of 10 and 90° to the interface plane. Afterwards, nanoindentation tests and Scanning Electron Microscopy (SEM) imaging coupled to an Energy Dispersive Spectroscopy (EDS) system were carried out across interfaces extending from the metal towards the porcelain area. Elemental diffusion profiles across the porcelain-to-metal interfaces were also obtained by EDS analysis. The mismatch in mechanical properties found in porcelain-to-Ti6Al4V interfaces was lower than that of porcelain-to-CP titanium. Cracking was noticed at low-thickness veneering dental porcelain regions after the nanoindentation tests of samples cross-sectioned at low angles to the interface plane. A wide reaction zone between titanium and porcelain as well as higher incidence of defects was noticed at the porcelain-to-CP titanium interfaces. This study confirmed Ti6Al4V as an improved alternative to CP-titanium as it showed to establish a better interface with the veneering dental porcelain considering the slight chemical interaction and the lower mechanical properties mismatch. The elastic modulus of porcelain-to-Ti6Al4V samples showed to be less sensitive to porcelain thickness variations.

Influence of the processing route of porcelain/Ti-6Al-4V interfaces on shear bond strength.

This study aims at evaluating the two-fold effect of initial surface conditions and dental porcelain-to-Ti-6Al-4V alloy joining processing route on the shear bond strength. Porcelain-to-Ti-6Al-4V samples were processed by conventional furnace firing (porcelain-fused-to-metal) and hot pressing. Prior to the processing, Ti-6Al-4V cylinders were prepared by three different surface treatments: polishing, alumina or silica blasting. Within the firing process, polished and alumina blasted samples were subjected to two different cooling rates: air cooling and a slower cooling rate (65°C/min). Metal/porcelain bond strength was evaluated by shear bond test. The data were analyzed using one-way ANOVA followed by Tuckey's test (p<0.05). Before and after shear bond tests, metallic surfaces and metal/ceramic interfaces were examined by Field Emission Gun Scanning Electron Microscope (FEG-SEM) equipped with Energy Dispersive X-Ray Spectroscopy (EDS). Shear bond strength values of the porcelain-to-Ti-6Al-4V alloy interfaces ranged from 27.1±8.9MPa for porcelain fused to polished samples up to 134.0±43.4MPa for porcelain fused to alumina blasted samples. According to the statistical analysis, no significant difference were found on the shear bond strength values for different cooling rates. Processing method was statistically significant only for the polished samples, and airborne particle abrasion was statistically significant only for the fired samples. The type of the blasting material did not cause a statistically significant difference on the shear bond strength values. Shear bond strength of dental porcelain to Ti-6Al-4V alloys can be significantly improved from controlled conditions of surface treatments and processing methods.