RESUMO
PURPOSE: To evaluate denture cleansing solutions regarding the surface roughness and color stability of two resilient liners with distinct optical characteristics used for the maximum recommended period of use. METHODS: The specimens of each resilient liner, transparent and white, were randomly distributed into groups (n= 15) of a daily 20-minute immersion simulation of 0.25%, 0.5% and 1% sodium hypochlorite (SH) and 4% acetic acid solutions. Surface roughness (Ra) and color stability (ΔE CIELab formula and NBS systems) were measured after 7, 14, 21, 30, 60, 90, 180, and 270 days. The factors of variations analyzed were material, solutions, and time of immersion. Statistical analysis used three-way ANOVA and Tukey tests (Ra), and repeated measure ANOVA (ΔE and NBS systems), P< 0.05. RESULTS: For Ra analysis, the variations occurred regardless of time and solution, as the white liner showed the greatest changes (P< 0.001). Regarding interactions between solution and time, in the period of 21 days until 270 days, Ra was equivalent for all solutions (P= 0.001). ΔE analysis showed a difference between solutions (P= 0.000) and interaction between time and solution (P= 0.000). For the transparent liner, the greatest changes were found for 1% SH after 60 days, however, at 270 days there was a color change equivalence with 0.5% SH, while 4% acetic acid solution showed intermediate values. For the white liner, 1% SH showed the highest color changes for all evaluated times, and the other evaluated solutions were similar after 270 days. For both resilient liners, 0.25% SH showed the smallest changes for the evaluated properties. CLINICAL SIGNIFICANCE: The changes found were dependent on the concentration of the solution used, as well as the length of exposure to the solution. In addition, the white resilient liner showed to be less susceptible to color changes. For both resilient liners, 0.25% sodium hypochlorite showed the least changes for the evaluated properties.
Assuntos
Higienizadores de Dentadura , Reembasadores de Dentadura , Acetatos , Resinas Acrílicas , Bases de Dentadura , Higienizadores de Dentadura/farmacologia , Teste de Materiais , Hipoclorito de Sódio/farmacologia , Propriedades de SuperfícieRESUMO
PURPOSE: To verify whether 0.1% and 0.2% sodium hypochlorite (NaOCl), and 8% Ricinus communis (RC) were able to remove denture biofilm without causing deleterious effects to acrylic resin. BACKGROUND: Previous data show that denture cleansers are effective in reducing biofilm; however, they can change acrylic resin properties. METHODS: In a crossover trial, 47 denture wearers brushed and soaked their dentures (20 min/14 d): control, 0.85% saline; SH1, 0.1% NaOCl; SH2, 0.2% NaOCl and RC. Denture biofilm on the intaglio surface was stained, photographed and quantified (Image Tool® ). Furthermore, 80 rectangular and 80 disc-shaped specimens (Lucitone 550) were assigned into tested solutions (n = 20), simulating 5 years of daily short immersions (20 minutes). A colorimeter and the National Bureau of Standards units (NBS) determined colour data (ΔE). Surface roughness and flexural strength were measured using rugosimeter and universal testing machine, respectively. Data were compared by the Friedman test (α = .05) followed by Wilcoxon, corrected by Bonferroni (α = .005) (clinical) and Kruskal-Wallis followed by the Dunn test (α = .05) (laboratorial). RESULTS: SH2 (MR=1.77) showed lower biofilm coverage; SH1 (MR = 2.37) and RC (MR = 2.74) presented intermediated values. RC (1.10 [0.96:1.75]) revealed higher colour alteration than SH1 (0.71 [0.62:0.80]) and SH2 (0.74 [0.58:0.85]); however, NBS classified all solutions as "trace" (0.0-0.5). There was no statistical significance for surface roughness (P = .760) and flexural strength (P = .547). CONCLUSIONS: The 0.2% NaOCl showed the best clinical performance and did not cause adverse effects on acrylic resin on laboratory analyses.