Mn52Al45.7C2.3 flakes with different sizes were prepared with two distinct surfactant-assisted ball-milling methods using cylindrical and barrel containers. Different microstructure and magnetic properties were measured based on the sequence of the container shape and different ball-milling times (2, 5, and 10 h). Morphology investigations showed that for powders milled in a barrel container, the amount of τ-phase was more compared to the samples milled in a cylindrical container. Moreover, in the powders milled with barrel containers, considerably higher magnetic properties were obtained in terms of saturation magnetization (Ms) and remanent magnetization (Mr) compared to those powders milled with cylindrical containers. Magnetic properties were found to be a function of the ball-milling time. High remanent magnetization and saturation magnetization have been found for powders milled in barrel containers, whereas only mediocre remanent magnetization and saturation magnetization have been measured in the case of milling in cylindrical containers. The highest Ms = 52.49 emu g-1 and Mr = 24.10 emu g-1 were obtained for the powders milled in barrel containers for 2 h. The higher magnetic properties taken from the milling in barrel containers is due to the higher shear stress and more uniform strain distribution induced by the barrel configuration, resulting in the stable τ-phase at a reasonably low-strain microstructure.
RESUMO
The reverse magnetization behavior for bulk composite alloys containing Mn-Al-C and α-Fe nanoparticles (NPs) has been investigated by hysteresis loops, recoil, and first-order reversal curves (FORC) analysis. The effect of adding different percentages of α-Fe (5, 10, 15, and 20 wt. %) on the magnetic properties and demagnetization behavior of Mn-Al-C nanostructured bulk magnets was investigated. The fabricated nanocomposites were characterized by XRD and VSM for structural analysis and magnetic behavior investigations, respectively. The demagnetization curve of the sample Mn-Al-C-5wt. % α-Fe showed a single hard magnetic behavior and showed the highest increase in remanence magnetization compared to the sample without α-Fe, and therefore this combination was selected as the optimal composition for FORC analysis. Magnetic properties for Mn-Al-C-5 wt. % α-Fe nanocomposite were obtained as Ms = 75 emu/g, Mr = 46 emu/g, Hc = 3.3 kOe, and (BH)max = 1.6 MGOe, indicating a much higher (BH)max than the sample with no α-Fe. FORC analysis was performed to identify exchange coupling for the Mn-Al-C-0.05α-Fe nanocomposite sample. The results of this analysis showed the presence of two soft and hard ferromagnetic components. Further, it showed that the reverse magnetization process in the composite sample containing 5 wt. % α-Fe is the domain rotation model.