RESUMO
Self-polarized energy harvesting materials have seen increasing research interest in recent years owing to their simple fabrication method and versatile application potential. In this study, we systematically investigated self-polarized P(VDF-TrFE)/carbon black (CB) composite thin films synthesized on flexible substrates, with the CB content varying from 0 to 0.6 wt.% in P(VDF-TrFE). The presence of -OH functional groups on carbon black significantly enhances its crystallinity, dipolar orientation, and piezoelectric performance. Multiple characterization techniques were used to investigate the crystalline quality, chemical structure, and morphology of the composite P(VDF-TrFE)/CB films, which indicated no significant changes in these parameters. However, some increase in surface roughness was observed when the CB content increased. With the application of an external force, the piezoelectrically generated voltage was found to systematically increase with higher CB content, reaching a maximum value at 0.6 wt.%, after which the sample exhibited low resistance. The piezoelectric voltage produced by the unpoled 0.6 wt.% CB composite film significantly exceeded the unpoled pure P(VDF-TrFE) film when subjected to the same applied strain. Furthermore, it exhibited exceptional stability in the piezoelectric voltage over time, exceeding the output voltage of the poled pure P(VDF-TrFE) film. Notably, P(VDF_TrFE)/CB composite-based devices can be used in energy harvesting and piezoelectric strain sensing to monitor human motions, which has the potential to positively impact the field of smart wearable devices.
RESUMO
Infrared transmission characteristics of VO2 thin films synthesized on multiple substrates, using a low-pressure direct oxidation technique, have been characterized. Material characterization of these films indicates high material quality, which resulted in large variation of electrical and optical properties at phase transition. A change in optical transmissivity greater than 80% was observed for these films utilizing infrared (IR) laser illumination at 1550 nm. Phase transition enabled by temperature change induced by a pulsed high-power laser beam resulted in modulated IR laser transmission with a low time constant in VO2 on transparent quartz and muscovite substrates. Investigation of the effect of mechanical strain on phase transition in VO2 grown on flexible muscovite substrate indicate shift in transition temperature to higher for tensile and lower for compressive strains.
RESUMO
Development of compact and fast modulators of infrared light has garnered strong research interests in recent years due to their potential applications in communication, imaging, and sensing. In this study, electric field induced fast modulation near-infrared light caused by phase change in VO2 thin films grown on GaN suspended membranes has been reported. It was observed that metal insulator transition caused by temperature change or application of electric field, using an interdigitated finger geometry, resulted in 7% and 14% reduction in transmitted light intensity at near-infrared wavelengths of 790 and 1550 nm, respectively. Near-infrared light modulation has been demonstrated with voltage pulse widths down to 300 µs at 25 V magnitude. Finite element simulations performed on the suspended membrane modulator indicate a combination of the Joule heating and electric field is responsible for the phase transition.