BACKGROUND: Treatment of young children under dental general anesthesia (DGA) is sometimes necessary due to lack of cooperation and the complexity of dental treatment. The aim of this study was to assess the changes in oral-health-related quality of life (OHRQoL) in children following treatment under DGA. METHODS: A consecutive sample of 88 children aged 5 and younger who were referred to the department of pediatric dentistry, Cairo university, Egypt, for treatment under DGA was included. Parents were asked to complete the Arabic version of the Early Childhood Oral Health Impact Scale (A-ECOHIS) questionnaire before and 4 weeks after treatment. The Wilcoxon signed-rank test was used to compare baseline and follow up scores. Effect sizes (ES) were also calculated. RESULTS: The overall ECOHIS scores decreased significantly from 16.72 (±7.07) to 0.9 (±3.08); (p < 0.001, Wilcoxon signed-rank test) after treatment under DGA, demonstrating a large effect size of 2.2. The scores of the two subscales of the ECOHIS, the child impact scale (CIS) and the family impact scale (FIS), also decreased significantly (p < 0.001). CONCLUSIONS: Treatment under DGA not only improved the OHRQoL of the Egyptian children in our sample significantly, but also had a positive effect on their families' quality of life.
RESUMO
OBJECTIVE: The aim of the study reported here was to evaluate the performance of a self-adhesive flowable composite and two self-etching adhesive systems, when subjected to cyclic loading, in preventing the nanoleakage of Class V restorations. METHODS: Wedge-shape Class V cavities were prepared (4×2×2 mm [length × width × depth]) on the buccal surfaces of 90 sound human premolars. Cavities were divided randomly into three groups (n=30) according to the used adhesive (Xeno(®) V [self-etching adhesive system]) and BOND-1(®) SF (solvent-free self-etching adhesive system) in conjunction with Artiste(®) Nano Composite resin, and Fusio™ Liquid Dentin (self-adhesive flowable composite), consecutively. Each group was further divided into three subgroups (n=10): (A) control, (B) subjected to occlusal cyclic loading (90N for 5,000 cycles), and (C) subjected to occlusal cyclic loading (90N for 10,000 cycles). Teeth then were coated with nail polish up to 1 mm from the interface, immersed in 50% silver nitrate solution for 24 hours and tested for nanoleakage using the environmental scanning electron microscopy and energy dispersive analysis X-ray analysis. Data were statistically analyzed using two-way analysis of variance and Tukey's post hoc tests (P≤0.05). RESULTS: The Fusio Liquid Dentin group showed statistically significant lower percentages of silver penetration (0.55 µ) compared with the BOND-1 SF (3.45 µ) and Xeno V (3.82 µ) groups, which were not statistically different from each other, as they both showed higher silver penetration. CONCLUSION: Under the test conditions, the self-adhesive flowable composite provided better sealing ability. Aging of the two tested adhesive systems, as a function of cyclic loading, increased nanoleakage.