Water Catchers within Sub-Nano Channels Promote Step-by-Step Zinc-Ion Dehydration Enable Highly Efficient Aqueous Zinc-Metal Batteries.

Zinc metal suffers from violent and long-lasting water-induced side reactions and uncontrollable dendritic Zn growth, which seriously reduce the coulombic efficiency (CE) and lifespan of aqueous zinc-metal batteries (AZMBs). To suppress the corresponding harmful effects of the highly active water, a stable zirconium-based metal-organic framework with water catchers decorated inside its sub-nano channels is used to protect Zn-metal. Water catchers within narrow channels can constantly trap water molecules from the solvated Zn-ions and facilitate step-by-step desolvation/dehydration, thereby promoting the formation of an aggregative electrolyte configuration, which consequently eliminates water-induced corrosion and side reactions. More importantly, the functionalized sub-nano channels also act as ion rectifiers and promote fast but even Zn-ions transport, thereby leading to a dendrite-free Zn metal. As a result, the protected Zn metal demonstrates an unprecedented cycling stability of more than 10 000 h and an ultra-high average CE of 99.92% during 4000 cycles. More inspiringly, a practical NH4V4O10//Zn pouch-cell is fabricated and delivers a capacity of 98 mAh (under high cathode mass loading of 25.7 mg cm-2) and preserves 86.2% capacity retention after 150 cycles. This new strategy in promoting highly reversible Zn metal anodes would spur the practical utilization of AZMBs.

Chelating Additive Regulating Zn-Ion Solvation Chemistry for Highly Efficient Aqueous Zinc-Metal Battery.

Aqueous zinc-metal batteries (AZMBs) usually suffered from poor reversibility and limited lifespan because of serious water induced side-reactions, hydrogen evolution reactions (HER) and rampant zinc (Zn) dendrite growth. Reducing the content of water molecules within Zn-ion solvation sheaths can effectively suppress those inherent defects of AZMBs. In this work, we originally discovered that the two carbonyl groups of N-Acetyl-ϵ-caprolactam (N-ac) chelating ligand can serve as dual solvation sites to coordinate with Zn2+, thereby minimizing water molecules within Zn-ion solvation sheaths, and greatly inhibit water-induced side-reactions and HER. Moreover, the N-ac chelating additive can form a unique physical barrier interface on Zn surface, preventing the harmful contacting with water. In addition, the preferential adsorption of N-ac on Zn (002) facets can promote highly reversible and dendrite-free Zn2+ deposition. As a result, Zn//Cu half-cell within N-ac added electrolyte delivered ultra-high 99.89 % Coulombic efficiency during 8000 cycles. Zn//Zn symmetric cells also demonstrated unprecedented long life of more than 9800 hours (over one year). Aqueous Zn//ZnV6O16 ⋅ 8H2O (Zn//ZVO) full-cell preserved 78 % capacity even after ultra-long 2000 cycles. A more practical pouch-cell was also obtained (90.2 % capacity after 100 cycles). This method offers a promising strategy for accelerating the development of highly efficient AZMBs.