RESUMO
Additive manufacturing of Alloy 718 has become a popular subject of research in recent years. Understanding the process-microstructure-property relationship of additively manufactured Alloy 718 is crucial for maturing the technology to manufacture critical components. Fatigue behaviour is a key mechanical property that is required in applications such as gas turbines. Therefore, in the present work, low cycle fatigue behaviour of Alloy 718 manufactured by laser beam powder bed fusion process has been investigated. The material was tested in as-built condition as well as after two different thermal post-treatments. Three orientations with respect to the building direction were tested to evaluate the anisotropy. Testing was performed at room temperature under controlled amplitudes of strain. It was found that defects, inclusions, strengthening precipitates, and Young's modulus influence the fatigue behaviour under strain-controlled conditions. The strengthening precipitates affected the deformation mechanism as well as the cycle-dependent hardening/softening behaviour. The defects and the inclusions had a detrimental effect on fatigue life. The presence of Laves phase in LB-PBF Alloy 718 did not have a detrimental effect on fatigue life. Young's modulus was anisotropic and it contributed to the anisotropy in strain-life relationship. Pseudo-elastic stress vs. fatigue life approach could be used to handle the modulus-induced anisotropy in the strain-life relationship.
RESUMO
Alloy 718 finds application in gas turbine engine components, such as turbine disks, compressor blades and so forth, due to its excellent mechanical and corrosion properties at elevated temperatures. Electron beam melting (EBM) is a recent addition to the list of additive manufacturing processes and has shown the capability to produce components with unique microstructural features. In this work, Alloy 718 specimens were manufactured using the EBM process with a single batch of virgin plasma atomized powder. One set of as-built specimens was subjected to solution treatment and ageing (STA); another set of as-built specimens was subjected to hot isostatic pressing (HIP), followed by STA (and referred to as HIP+STA). Microstructural analysis of as-built specimens, STA specimens and HIP+STA specimens was carried out using optical microscopy and scanning electron microscopy. Typical columnar microstructure, which is a characteristic of the EBM manufactured alloy, was observed. Hardness evaluation of the as-built, STA and HIP+STA specimens showed that the post-treatments led to an increase in hardness in the range of ~50 HV1. Tensile properties of the three material conditions (as-built, STA and HIP+STA) were evaluated. Post-treatments lead to an increase in the yield strength (YS) and the ultimate tensile strength (UTS). HIP+STA led to improved elongation compared to STA due to the closure of defects but YS and UTS were comparable for the two post-treatment conditions. Fractographic analysis of the tensile tested specimens showed that the closure of shrinkage porosity and the partial healing of lack of fusion (LoF) defects were responsible for improved properties. Fatigue properties were evaluated in both STA and HIP+STA conditions. In addition, three surface conditions were also investigated, namely the 'raw' as-built surface, the machined surface with the contour region and the machined surface without the contour region. Machining off the contour region completely together with HIP+STA led to significant improvement in fatigue performance.