RESUMO
In this study, we investigate the effect of small amounts of zirconium alloying the medium-entropy alloy (TiVNb)85Cr15, a promising material for hydrogen storage. Alloys with 1, 4, and 7 at.% of Zr were prepared by arc melting and found to be multiphase, comprising at least three phases, indicating that Zr addition does not stabilize a single-phase solid solution. The dominant BCC phase (HEA1) is the primary hydrogen absorber, while the minor phases HEA2 and HEA3 play a crucial role in hydrogen absorption/desorption. Among the studied alloys, Zr4 (TiVNb)81Cr15Zr4 shows the highest hydrogen storage capacity, ease of activation, and reversibly retrievable hydrogen. This alloy can absorb hydrogen at room temperature without additional processing, with a reversible capacity of up to 0.74 wt.%, corresponding to hydrogen-to-metal ratio H/M = 0.46. The study emphasizes the significant role of minor elemental additions in alloy properties, stressing the importance of tailored compositions for hydrogen storage applications. It suggests a direction for further research in metal hydride alloys for effective and safe hydrogen storage.
RESUMO
This study focuses on the preparation and characterization of zinc-based alloys containing magnesium, calcium, and manganese. The alloys were prepared by the melting of pure elements, casting them into graphite molds, and thermo-mechanically treating them via hot extrusion. The phase compositions of the samples were analyzed using X-ray diffraction technique and SEM/EDX analysis. The analysis confirmed that in addition to the Zn matrix, the materials are reinforced by the CaZn13, MgZn2, and Mn-based precipitates. The mechanical properties of the alloys were ascertained by tensile, compressive, and bending tests, measurement of the samples microhardness and elastic modulus. The results indicate that an increase in Mn content leads to an increase in the maximum stress experienced under both tension and compression. However, the plastic deformation of the alloys decreases with increasing Mn content. This study provides valuable insights into the microstructural changes and mechanical behavior of zinc-based alloys containing magnesium, calcium, and manganese, which can be used to design alloys for specific biomedical applications.
RESUMO
This paper deals with the tribological study of the laser remelted surfaces of the ECAP-processed AZ61 magnesium alloy and AZ61-Al2O3 metal matrix composite with 10 wt.% addition of Al2O3 nanoparticles. The study included the experimental optimization of the laser surface remelting conditions for the investigated materials by employing a 400 W continual wave fiber laser source. Tribological tests were performed in a conventional "ball-on-disc" configuration with a ceramic ZrO2 ball under a 5 N normal load and a sliding speed of 100 mm/s. The results showed that both the incorporation of Al2O3 nanoparticles and the applied laser treatments led to recognizable improvements in the tribological properties of the studied AZ61-Al2O3 composites in comparison with the reference AZ61 alloy. Thus, the best improvement has been obtained for the laser modified AZ61-10 wt.% Al2O3 nanocomposite showing about a 48% decrease in the specific wear rate compared to the laser untreated AZ61 base material.